The invention discloses a preparation method of propanoic acid chromium, the method comprises the following steps: the salt forming reaction steps: propanoic acid, chromium oxide, initiator, water into reactor, stirring, heating reaction, carbon dioxide is generated to overflow, the propionic acid chromium; drying steps: knot granular product crystal separation the drying screen on the upper and lower permeability, drying. The product is screened and the product is obtained. The present invention in the production process, the use of chromium oxide and the initiator, ensure the granular products, to dry, not crushed, avoid dust, and the invention has the advantages of simple, convenient operation, saving equipment investment, improve production efficiency.
【技术实现步骤摘要】
一种正丙酸铬的制备方法
本专利技术属于有机化合物制备领域,尤其是一种正丙酸铬简便,有效的制备方法。
技术介绍
在有机添加剂中,正丙酸铬做为一种有效的铬矿物添加剂,越来越受到重视,具有广泛的应用前景。正丙酸铬的通常生产方法是利用正丙酸钠与硫酸铬反应,得到的产品为粘稠状物,进一步处理困难,难以提纯,此类制备方法存在的问题:1,进一步处理步骤中,多次结晶,需增加结晶设备,设备多,复杂生产成本高,难以降低生产成本;2,成品纯度低,粉尘很多,企业难以大量生产,不利于企业的发展和经济效益的提高。
技术实现思路
本专利技术的目的在于克服现有技术的不足,提供了一种能够节约设备投资、降低成本,得到的产品无需多次结晶,避免了大量的重复的劳动的一种正丙酸铬的制备方法。本专利技术解决其技术问题是采用以下技术方案实现:一种正丙酸铬的制备方法,其特征在于,该方法包括以下步骤:⑴成盐反应步骤将正丙酸,氧化铬,引发剂,水投入反应釜中,搅拌,加热反应,使二氧化碳溢出,生成正丙酸铬;⑵烘干步骤将结晶分离得到的颗粒状产品,于上下透气的干燥筛中,烘干。得到的产品过筛,得到产品。而且,所述的引发剂为具有CnHn+2NmHm+2[n=1,2,3,4,5,6;m=1,2]胺类化合物。而且,所述的胺类化合物和正丙酸的摩尔比为0.2—0.5:1。而且,所述的正丙酸,水,氧化铬的摩尔比为2:30:1.3—1.65。而且,所述的上下透气的干燥筛为不锈钢筛。本专利技术的优点和积极效果是:1、本正丙酸铬的制备方法在投料中,使用正丙酸代替正丙酸钠,使用氧化铬代替硫酸铬,得到的产品只有正丙酸铬,产品单一,纯度高,呈颗粒状 ...
【技术保护点】
一种正丙酸铬的制备方法,其特征在于:该方法包括以下步骤:⑴成盐反应步骤将正丙酸,氧化铬,引发剂,水投入反应釜中,搅拌,加热反应,使二氧化碳溢出,生成正丙酸铬;⑵烘干步骤将结晶分离得到的颗粒状产品,于上下透气的干燥筛中,烘干;得到的产品过筛,得到产品。
【技术特征摘要】
1.一种正丙酸铬的制备方法,其特征在于:该方法包括以下步骤:⑴成盐反应步骤将正丙酸,氧化铬,引发剂,水投入反应釜中,搅拌,加热反应,使二氧化碳溢出,生成正丙酸铬;⑵烘干步骤将结晶分离得到的颗粒状产品,于上下透气的干燥筛中,烘干;得到的产品过筛,得到产品。2.根据权利要求1所述的正丙酸铬的制备方法,其特征在于:所述的引发剂为具有CnHn+2NmHm+2[n=1,...
【专利技术属性】
技术研发人员:张富强,
申请(专利权)人:天津市化学试剂研究所有限公司,
类型:发明
国别省市:天津,12