一种三氟氧钛酸铵及其制备和应用制造技术

本发明专利技术属于电池材料制备领域，具体涉及一种三氟氧钛酸铵及其制备和应用。先以氟化铵、钛酸四丁酯为原料，通过水热合成方法制得实心立方块形状的三氟氧钛酸铵。然后将该三氟氧钛酸铵作为散射层印刷在商业化TiO2层上，再将该光阳极膜经过硼酸溶液浸泡处理，使三氟氧钛酸铵转化为空心结构的二氧化钛立方块，从而提高电池的光电转化效率。

A kind of ammonium three fluoro titanate and its preparation and Application

The invention belongs to the field of preparation of battery materials, in particular to a kind of three ammonium peroxytitanate and its preparation and application. A solid cubic block of ammonium perfluoro titanate was prepared by hydrothermal synthesis by using ammonium fluoride and four butyl titanate as raw materials. Then, the three fluoro titanate is printed on the commercial TiO2 layer as the scattering layer, and then the photoanode film is soaked in boric acid solution to transform the three fluoro titanate to the hollow structure of the titanium dioxide cubic block, thereby improving the photoelectric conversion efficiency of the battery.

【技术实现步骤摘要】
一种三氟氧钛酸铵及其制备和应用
本专利技术属于电池材料制备领域，具体涉及一种三氟氧钛酸铵及其制备和应用。
技术介绍
染料敏化太阳能电池自开发出来就因其众多的优点引来各国研究工作者的密切关注，这种电池低成本、高光电转换效率、对环境无污染，非常有可能替代硅晶电池成为下一代光伏产业的支柱产品。TiO2半导体材料在染料吸附、电荷分离及传输等方面都显示了优异的性能，因此在目前的研究结果中，TiO2是性能最优越的光阳极材料。此外，TiO2具有化学稳定性良好，耐强酸强碱能力强等优势，这对电池器件的长期稳定性来说是十分重要的。近年来，设计和合成分等级结构TiO2成为新一轮的研究热点，这是由于分等级结构材料在提供散射作用的同时，保持了高比表面积。但是，一般分等级结构TiO2的制备比较复杂，重现性低，且制备得到的样品比表面积和散射效果不太理想。三氟氧钛酸铵主要是通过氟钛酸铵（(NH4)2TiF6）和硼酸（H3BO3）反应制得，所得颗粒大小不一，形状不规整，不利于后期拓扑转化以制得{001}面暴露在外的二氧化钛材料。为了控制其大小以及形状，往往需要在反应体系中加入表面活性剂，这无形中又增加了制备成本。同时本文档来自技高网...

【技术保护点】
一种三氟氧钛酸铵的制备方法，其特征在于：将20mL‑30mL冰醋酸和5‑10mmol氟化铵混合，搅拌使氟化铵完全溶解，得混合溶液；然后将0.5‑1.5mL钛酸四丁酯逐滴加入混合溶液中，继续搅拌反应15min；将反应体系转移到高压反应釜中，置于140‑160℃烘箱中恒温反应8‑16h后得白色沉淀，将白色沉淀离心分离，用去离子水和乙醇洗涤后得到实心立方块形状的三氟氧钛酸铵。

【技术特征摘要】
1.一种三氟氧钛酸铵的制备方法，其特征在于：将20mL-30mL冰醋酸和5-10mmol氟化铵混合，搅拌使氟化铵完全溶解，得混合溶液；然后将0.5-1.5mL钛酸四丁酯逐滴加入混合溶液中，继续搅拌反应15min；将反应体系转移到高压反应釜中，置于140-160℃烘箱中恒温反应8-16h后得白色沉淀，将白色沉淀离心分离，用去离子水和乙醇洗涤后得到实心立方块形状的三氟氧钛酸铵。2.一种利用权利要求1所述的三氟氧钛酸铵作为散射层的光阳极膜的制备方法，其特征在于：具体步骤为：1）将三氟氧钛酸铵、乙基纤维素和松油醇按20:2:1重量比混合均匀，然后加入200...

【专利技术属性】
技术研发人员：魏明灯，谢锋炎，李亚峰，
申请(专利权)人：福州大学，
类型：发明
国别省市：福建,35