The invention discloses a non autoclaved aerated brick, including: 1050, 1000 weathering powder fly ash 400 500 copies, 800 copies, 600 slag cement 100 150 copies, 80 copies, 50 gypsum powder 30 40 copies, 20 copies, 10 mg white latex 25 30 continuous and non autoclaved foaming agent 80 160. The non steamed pressure adding brick with no steam pressure strong foaming agent, its performance is neutral, and water has a good affinity. A large number of bubbles are produced in the cement slurry, and the autoclaved aerated brick has good insulation and sound insulation effect. Non autoclaved strong foaming agent uses no pollution animal protein and plant protein. It will not produce any negative effects on producers, users or environment. The energy consumption of the building building materials is greatly reduced, and the performance of the prepared gas brick is excellent.
【技术实现步骤摘要】
一种免蒸压加气砖
本专利技术涉及建材
，具体为一种免蒸压加气砖。
技术介绍
加气混凝土砌块即通过蒸压加气制成的混凝土块，简称加气砖，是通过高温蒸压设备工艺生产的加气混凝土砌块。“加气砖”可以理解为一个简化的或是一个通用的名称。其涵盖的产品范围应该要大一点，即采用包括蒸压在内的其他各种工艺生产的砖品。加气砖具有自重轻、保温隔热性能好、抗震能力强、加工性能好等特点。传统加气砖需要用进行高温蒸压，使得加气砖生产消耗能源大，需要进一步降低加气砖生产的能源消耗。
技术实现思路
本专利技术的目的在于降低传统加气砖生产的能源消耗，达到节约资源，节能环保的目的，提供一种免蒸压加气砖。为达到上述目的，采用的技术方案为：一种免蒸压加气砖，包含的组份及重量比是：风化石粉1000-1050份、煤灰粉400-500份、矿渣粉600-800份、水泥100-150份、石膏50-80份、铝粉30-40份、镁粉10-20份、白乳胶25-30份以及免蒸压发泡剂80-160份。进一步，所述的免蒸压加气砖，包含的组份及重量比特征是：风化石粉1040份、煤灰粉450份、矿渣粉650份、水泥130份、石膏60份、铝粉35份、镁粉15份、白乳胶28份以及免蒸压发泡剂130份。采用上述方案的有益效果为：这种免蒸压加气砖采用免蒸压强力发泡剂，其性能为中性，与水有很好的亲和性。在水泥浆中产生大量的气泡，蒸压加气砖具有良好的保温隔热隔音效果。免蒸压强力发泡剂使用无污染的动物蛋白质和植物蛋白质，无论是对生产者还是使用者及环境都不会产生任何负作用。使得加气砖建材生产的能源消耗大大降低，制备的加气砖性能优异。具体...
【技术保护点】
一种免蒸压加气砖，包含的组份及重量比特征是：风化石粉1000‑1050份、煤灰粉 400‑500份、矿渣粉 600‑800份、水泥 100‑150份、石膏50‑80份、铝粉30‑40份、镁粉 10‑20份、白乳胶25‑30份以及免蒸压发泡剂80‑160份。
【技术特征摘要】
1.一种免蒸压加气砖，包含的组份及重量比特征是：风化石粉1000-1050份、煤灰粉400-500份、矿渣粉600-800份、水泥100-150份、石膏50-80份、铝粉30-40份、镁粉10-20份、白乳胶25-30份以及免蒸...
【专利技术属性】
技术研发人员：陈志华，
申请(专利权)人：遵义翔辉环保产业有限责任公司，
类型：发明
国别省市：贵州,52