The invention discloses a building waste regeneration brick and a preparation method, which belongs to the technical field of building materials. It consists of the following parts by weight of raw materials: recycled aggregate 20 40 copies, 20 copies of the 10 reinforcing agent and water reducing agent 5 15 copies, 20 copies, 10 curing agent bamboo fiber 5 15 copies, 30 copies, 10 Portland cement 30 water 60, fly ash 5 15 copies and 20 copies of polyamide 10. The building waste regeneration brick and tile of the invention has high strength, stable quality, long service life and low cost, which can turn waste into treasure, environmental protection and energy saving, and has good economic benefits and wide social benefits.
【技术实现步骤摘要】
一种建筑垃圾再生砖瓦及其制备方法
本专利技术涉及一种建筑垃圾再生砖瓦及其制备方法，属于建筑材料
技术介绍
建筑垃圾是城市垃圾的主要组成部分。当前对待建筑垃圾以传统的露天堆放、深挖填埋为主，这种方式虽然处理量大、方便简单、处理费用低，但实际是占用了土地资源。建筑垃圾若不能及时回收利用，不仅污染环境，还造成了资源浪费。
技术实现思路
本专利技术的目的之一，是提供一种建筑垃圾再生砖瓦。本专利技术的建筑垃圾再生砖瓦强度高，质量稳定，使用寿命长，成本低，能够变废为宝，环保节能，具有很好的经济效益和广泛的社会效益本专利技术解决上述技术问题的技术方案如下：一种建筑垃圾再生砖瓦，由如下重量份数的原料制成：建筑垃圾再生骨料20-40份、增强剂10-20份、减水剂5-15份、固化剂10-20份、竹纤维5-15份、硅酸盐水泥10-30份、水30-60份、粉煤灰5-15份和聚酰胺10-20份。在上述技术方案的基础上，本专利技术还可以做如下改进。进一步，由如下重量份数的原料制成：建筑垃圾再生骨料30份、增强剂15份、减水剂10份、固化剂15份、竹纤维10份、硅酸盐水泥20份、水45份...
【技术保护点】
一种建筑垃圾再生砖瓦，其特征在于，由如下重量份数的原料制成：建筑垃圾再生骨料20‑40份、增强剂10‑20份、减水剂5‑15份、固化剂10‑20份、竹纤维5‑15份、硅酸盐水泥10‑30份、水30‑60份、粉煤灰5‑15份和聚酰胺10‑20份。
【技术特征摘要】
1.一种建筑垃圾再生砖瓦，其特征在于，由如下重量份数的原料制成：建筑垃圾再生骨料20-40份、增强剂10-20份、减水剂5-15份、固化剂10-20份、竹纤维5-15份、硅酸盐水泥10-30份、水30-60份、粉煤灰5-15份和聚酰胺10-20份。2.根据权利要求1所述的一种建筑垃圾再生砖瓦，其特征在于，由如下重量份数的原料制成：建筑垃圾再生骨料30份、增强剂15份、减水剂10份、固化剂15份、竹纤维10份、硅酸盐水泥20份、水45份、粉煤灰10份和聚酰胺15份。3.根据权利要求1或2所述的一种建筑垃圾再生砖瓦，其特征在于，所述建筑垃圾再生骨料是指经粉碎、筛分、剔除杂物后得到的粒径为2-10mm的建筑垃圾。4.根据权利要求1或2所述的一种建筑垃圾再生砖瓦，其特征在于，所述增强剂为硅灰粉和可再分散乳胶粉按质量比1:5的混...
【专利技术属性】
技术研发人员：黄云鸿，李力，
申请(专利权)人：桂林市春晓环保科技有限公司，
类型：发明
国别省市：广西,45