The present invention provides a method for machining of cast iron, relates to the technical field of mechanical processing, which comprises the following steps: (1) the first 600 cast iron is heated to 650 DEG C, and maintain 30 35 minutes; (2) the iron temperature in half a minute rapid cooling to 400 450 DEG C, and in the temperature range 400 450 C 20 maintained within 25 minutes; (3) and then cast half a minute to 700 rapidly heated to 730 DEG C, machining in the temperature range of 730 DEG C within 700. In the invention, the invention of cast iron cold and hot, the casting internal stress release, can effectively avoid casting fracture in the process; at the same time mechanical processing in 700 temperature of 730 DEG C, by casting in the overall state of high fever and hardness of cast iron is greatly reduced, so the local produce mechanical processing the heat can be ignored, will not cause damage to the casting deformation.
【技术实现步骤摘要】
一种铸铁的机械加工方法
本专利技术涉及机械加工
，具体涉及一种铸铁的机械加工方法。
技术介绍
铸铁主要由铁、碳和硅组成的合金的总称。在这些合金中，含碳量超过在共晶温度时能保留在奥氏体固溶体中的量。为了将铸铁应用于机械部件，还需要对铸铁进行机械加工，现有铸铁的机械加工方法存在以下技术问题：1、在常温下进行，对铸铁进行加工时由于加工局部热量的产生，会使铸铁存在一定的形变；2、铸件内部应力释放不完全，产生的扭力作用大，容易在加工过程中断裂，比如采用普通的铣刀磨削加工工艺无法满足高精度的梯度加工要求，加工成品率低。
技术实现思路
本专利技术提供一种铸铁的机械加工方法，以解决现有铸铁的机械加工方法存在的加工形变大、因铸件内部应力释放不完全而造成加工成品率低的技术问题。为解决上述技术问题，本专利技术采用以下技术手段：一种铸铁的机械加工方法，包括如下步骤：(1)先将铸铁加热至600-650℃，并维持30-35分钟；(2)将铸铁温度在半分钟内迅速降温至400-450℃，并在400-450℃的温度范围内维持20-25分钟；(3)再将铸铁半分钟内迅速加热至700-730℃后，在70...
【技术保护点】
一种铸铁的机械加工方法，其特征在于，包括如下步骤：(1)先将铸铁加热至600‑650℃，并维持30‑35分钟；(2)将铸铁温度在半分钟内迅速降温至400‑450℃，并在400‑450℃的温度范围内维持20‑25分钟；(3)再将铸铁半分钟内迅速加热至700‑730℃后，在700‑730℃的温度范围内进行机械加工。
【技术特征摘要】
1.一种铸铁的机械加工方法，其特征在于，包括如下步骤：(1)先将铸铁加热至600-650℃，并维持30-35分钟；(2)将铸铁温度在半分钟内迅速降温至400-...