The invention discloses a testing method for the bonding property of iron ore, which belongs to the field of sintering technology. The method comprises: adding hydrated lime mixed with water, stirring to obtain lime suspension; the iron ore powder and the lime suspension mixing, stirring to obtain mixed suspension; or use the rheometer viscometer test suspension viscosity, bonding properties of the iron ore powder. Thus, it is effective to solve the problem that it is difficult to quantitatively measure the bonding performance of iron ore in the existing technology. By testing the bonding properties of different iron ore powders at different temperatures, it provides a reference for reasonable matching of all kinds of iron ore powder to obtain good pelletizing effect.
【技术实现步骤摘要】
一种铁矿粉粘结性能的测试方法
本专利技术涉及烧结
,特别涉及一种铁矿粉粘结性能的测试方法。
技术介绍
铁矿粉烧结过程中的制粒效果直接影响烧结过程料层透气性,对烧结料层厚度设置、烧结速度及烧结矿质量均有重要影响。烧结原料制粒效果的影响因素中,目前关注较多的是水、生石灰及混合机参数设置等因素,而烧结用铁矿粉少则3-5种,多则十几种,矿粉种类及粘结特性对制粒过程的影响很大,而铁矿粉粘结特性的测试和研究方法尚未得到关注,难以定量衡量铁矿粉粘结性能及评价铁矿粉对于制粒效果的影响。
技术实现思路
本专利技术通过提供一种铁矿粉粘结性能的测试方法,解决了现有技术中难以定量衡量铁矿粉粘结性能的问题。为解决上述技术问题,本专利技术提供了一种铁矿粉粘结性能的测试方法,包括:将熟石灰与水混合,搅拌获得熟石灰悬浊液;将铁矿粉与所述熟石灰悬浊液混合,搅拌获得混合悬浊液;使用流变仪或粘度计测试所述混合悬浊液的粘度,获得所述铁矿粉的粘结性能。进一步地,所述铁矿粉、熟石灰和水的质量比为2:1:1。进一步地,所述铁矿粉为粒度1mm以下的精矿粉或经筛分后粒度1mm以下的富矿粉。进一步地,所述搅拌的转 ...
【技术保护点】
一种铁矿粉粘结性能的测试方法,其特征在于,包括:将熟石灰与水混合,搅拌获得熟石灰悬浊液;将铁矿粉与所述熟石灰悬浊液混合,搅拌获得混合悬浊液;使用流变仪或粘度计测试所述混合悬浊液的粘度,获得所述铁矿粉的粘结性能。
【技术特征摘要】
1.一种铁矿粉粘结性能的测试方法,其特征在于,包括:将熟石灰与水混合,搅拌获得熟石灰悬浊液;将铁矿粉与所述熟石灰悬浊液混合,搅拌获得混合悬浊液;使用流变仪或粘度计测试所述混合悬浊液的粘度,获得所述铁矿粉的粘结性能。2.如权利要求1所述的铁矿粉粘结性能的测试方法,其特征在于,所述铁矿粉、熟石灰和水的质量比为2:1:1。3.如权利要求1或2所述的铁矿粉粘结性能的测试方法,其特征在于,所述...
【专利技术属性】
技术研发人员:马怀营,潘文,赵志星,裴元东,梁洁,张晓臣,马泽军,徐萌,李玉奇,左广传,赵勇,陈绍国,李荣昇,
申请(专利权)人:首钢集团有限公司,
类型:发明
国别省市:北京,11