The invention belongs to the field of synthetic leather, in particular to an environmentally friendly low VOC leather, from top to bottom comprises a first resin layer, a second resin layer and the base cloth layer, the resin layer is composed of a number of 85 quality 92 copies 0.8 copies of 0.2 polyurethane material, thickening agent, defoaming agent 0.1 0.6 30 and 3 activated carbon, the activated carbon after acidic or alkaline solution soaking, washing, and drying. The product prepared by the invention has the advantages of environmental protection, low consumption and excellent performance, and is easy to batch production.
【技术实现步骤摘要】
一种环保型低VOC人造革
本专利技术涉及合成革领域，具体涉及一种环保型低VOC人造革。
技术介绍
PVC人造革上箱包、沙发、汽车坐垫等皮革制品等理想材料，但增塑剂但大量使用及耐油性差、手感差而限制其应用。PU/PVC合成革弥补了PVC人造革但缺点，拥有和PU合成革同等的耐油性、触感及面层PU阻止PVC中间发泡层中增塑剂向表面迁移，并且其产品价格比PU合成革价格低廉。但传统PU面层树脂中含有70％以上但挥发性溶剂，导致环境污染严重。VOC，即挥发性有机化合物，对人体健康有巨大影响。当密闭空间中的VOC达到一定浓度时，短时间内人们会感到头痛、恶心、呕吐、乏力等，严重时会出现抽搐、昏迷，并会伤害到人的肝脏、肾脏、大脑和神经系统，造成记忆力减退等严重后果，而现有的人造皮革在制造过程中会残留部分VOC，皮革长期暴露在空气中，随着外界温度等环境因素的变化，皮革中的VOC很容易挥发至空气中，影响人体健康。目前，皮革制品中残存的VOC，主要是通过添加去醛基材料层的方式将挥发性有机物质包裹在皮革层中，但随着皮革制品的老化，其中包裹的挥发性有机物质容易慢慢扩散。
技术实现思路
基于背景技...
【技术保护点】
一种环保型低VOC人造革，自上而下依次包括第一树脂层、第二树脂层和基布层，其特征在于，所述树脂层均由质量份数为85‑92份聚氨酯材料、0.2‑0.8份增稠剂、0.1‑0.6份消泡剂和3‑30份活性炭组成，其中活性炭为经过改性的活性炭。
【技术特征摘要】
1.一种环保型低VOC人造革，自上而下依次包括第一树脂层、第二树脂层和基布层，其特征在于，所述树脂层均由质量份数为85-92份聚氨酯材料、0.2-0.8份增稠剂、0.1-0.6份消泡剂和3-30份活性炭组成，其中活性炭为经过改性的活性炭。2.根据权利要求1所述的一种环保型低VOC人造革，其特征在于，所述改性的活性炭为经过酸改性的活性炭和/或经过碱改性的活性炭。3.根据权利要求2所述的一种环保型低VOC人造革，其特征在于，所述经过酸改性的活性炭的制备过程包括以下步骤：(1)配置酸性溶液；(2)称取活性炭，并浸泡于酸性溶液中；(3)将浸泡后的活性炭取出，用蒸馏水冲洗；(4)取步骤(3)冲洗后的活性炭并烘干，制得所需活性炭。4.根据权利要求2所述的一种环保型低VOC人造革，其特征在于，所述经过碱改性的活性炭的制备过程包括以下步骤：(1)配置碱性溶液；(2)称取活性炭，并浸泡于碱性溶液中；(3)将浸泡后的活性炭取出，用蒸馏水冲洗；(4)取步骤(3)冲洗后的活性炭并烘干，制得所需活性炭...
【专利技术属性】
技术研发人员：赵建明，徐青，徐雪明，
申请(专利权)人：昆山阿基里斯人造皮有限公司，
类型：发明
国别省市：江苏,32