The present invention discloses a kind of ultra high strength steel yoke, its chemical composition according to the weight percentage of C:0.10 ~ 0.15, Si: 0.15, Mn:1.85 ~ 2, P = 0.015, S = 0.010, Ti:0.20 ~ 0.30, Nb:0.05 ~ 0.07, Mo:0.35 ~ 0.55, B:0.001 ~ 0.003, Als:0.02 ~ 0.10. N: = 0.010, the rest of Fe and unavoidable inclusion. The present invention in order to further improve the strength, and effectively break through the limit strength of 700MPa steel 700MPa ferrite, the invention by way of strengthening organization, namely adding bainite forming elements according to the invention, with the ultra fast cooling process, obtain bainite, obtain ultra high strength steel yoke.
【技术实现步骤摘要】
一种超高强度磁轭钢及其制造方法
本专利技术涉及微合金化钢制造领域，具体地指一种超高强度磁轭钢及其制造方法。
技术介绍
中国的水电和煤炭能源储备处于大体相同的水平，而水电资源是一种清洁无污染、可再生的资源，因而开发水电建设对于缓解我国电力紧张，实现可持续发展有着巨大的现实意义。根据我国水电开发的规划，未来在西藏地区的开发潜力巨大，而根据西藏地区的独特地形地貌，修建的水电站均为高水头水电站，因而要求水轮发电机中转子磁轭部分用钢的屈服强度进一步提升到900MPa以上，同时还要求具有良好的磁性能。在本专利技术申请之前，已有专利号为ZL200710051252.7和200710051251.2的专利技术专利记载了“C-Mn-Ti系热轧高强度高磁感性能钢及其制造方法”和“C-Mn-Ti-Nb系热轧高强度高磁感性能钢及其制造方法”，这两项专利分别介绍了采用控轧控冷方法生产的C-Mn-Ti系及C-Mn-Ti-Nb系热轧磁轭钢，屈服强度分别为ReL≥600MPa和ReL≥700MPa，其强度远低于900MPa。专利申请号为201610867421.3专利技术专利记载了“一种CSP流...
【技术保护点】
一种超高强度磁轭钢，其特征在于它的化学成份按重量百分数计为C：0.10～0.15，Si：≤0.15，Mn：1.85～2.00，P：≤0.015，S：≤0.010，Ti：0.20～0.30，Nb：0.05～0.07，Mo：0.35～0.55，B：0.001～0.003，Als：0.02～0.10，N：≤0.010，其余为Fe及不可避免的夹杂。
【技术特征摘要】
1.一种超高强度磁轭钢，其特征在于它的化学成份按重量百分数计为C：0.10～0.15，Si：≤0.15，Mn：1.85～2.00，P：≤0.015，S：≤0.010，Ti：0.20～0.30，Nb：0.05～0.07，Mo：0.35～0.55，B：0.001～0.003，Als：0.02～0.10，N：≤0.010，其余为Fe及不可避免的夹杂。2.根据权利要求1所述的一种超高强度磁轭钢，其特征在于它的化学成份按重量百分数计为C：0.10～0.15，Si：≤0.15，Mn：1.85～2.00，P：≤0.015，S：≤0.010，Ti：0.20～0.25，Nb：0.05～0.07，Mo：0.40～0.50，B：0.002～0.003，Als：0.02～0.10，N：≤0.010，其余为Fe及不可避免的夹杂。3.根据权利要求1所述的一种超高强度磁轭钢，其特征在于它的屈服强度≥900MPa，抗拉强度≥980MPa，延伸率A≥10...
【专利技术属性】
技术研发人员：宋畅，胡唐国，毛新平，陶文哲，毛传军，陈吉清，徐进桥，刘昌明，高智平，