一种木建筑承重梁柱及其生产方法技术

本发明专利技术公开了一种木建筑承重梁柱及其生产方法，所述木建筑承重梁柱包括卷曲成多层结构的木材单板和玻璃纤维无纺布，所述木材单板与玻璃纤维无纺布之间通过异氰酸酯或者环氧树脂类胶粘剂粘接。本发明专利技术利用玻璃纤维优异的抗拉伸性能，与具有优良强重比的木质材料结合，以异氰酸酯或者环氧树脂类结构用胶粘剂将两者复合在一起，以缠绕卷曲的方式形成多层结构，增加了梁柱材料的强度，使本发明专利技术木建筑承重梁柱具有性能稳定、强度高、自重轻的特点。

A wooden building bearing beam column and its production method

The invention discloses a wooden building load-bearing beam column and its production method, the wooden building load-bearing beam column including coiled wood veneer multi-layer structure and glass fiber non-woven fabric between the veneer and the glass fiber cloth or epoxy resin adhesive with isocyanate adhesive. The invention uses glass fiber excellent tensile properties, with excellent strength to weight ratio of the wood materials, with isocyanate epoxy resin structural adhesive or combined together, a multilayer structure formed by winding coil, increase the intensity of the beam column material, the wooden building load-bearing beam columns with the characteristics of stable performance, high strength and light weight.

【技术实现步骤摘要】
一种木建筑承重梁柱及其生产方法
本专利技术涉及木质建筑材料制造
，更具体地说，尤其涉及一种木建筑承重梁柱及其生产方法。
技术介绍
目前，在建筑行业，承重用梁柱大多为钢筋混凝土结构，浇注钢筋混凝土所用的钢筋、水泥等材料在生产中大量消耗能源并且容易产生环境污染，同时钢筋混凝土的自身重量较重。而木材本身是公认的具有高强重比的建筑材料，但是由于原木本身存在的易开裂特性，使得木材在作为承重梁使用时受到限制。
技术实现思路
本专利技术的目的在于针对上述现有技术的不足，提供一种性能稳定、强度高、自重轻的木建筑承重梁柱。为实现上述目的，本专利技术采用的技术方案是：一种木建筑承重梁柱，包括卷曲成多层结构的木材单板和玻璃纤维无纺布，所述木材单板与玻璃纤维无纺布之间通过异氰酸酯或者环氧树脂类胶粘剂粘接。本专利技术还提供了上述木建筑承重梁柱的生产方法，包括以下步骤：1)将旋切后的木材单板干燥至含水率8-10%，将干燥后的单板按要求拼宽（宽度等于梁柱的高度），将单板以同样规格幅面整张化后展平并加压堆垛，储存备用；2)在单板表面涂覆异氰酸酯或者环氧树脂类胶粘剂，将网状玻璃纤维无纺布粘附在单板上，并将单板逐张接本文档来自技高网...

【技术保护点】
一种木建筑承重梁柱，其特征在于：包括卷曲成多层结构的木材单板和玻璃纤维无纺布，所述木材单板与玻璃纤维无纺布之间通过异氰酸酯或者环氧树脂类胶粘剂粘接。

【技术特征摘要】
1.一种木建筑承重梁柱，其特征在于：包括卷曲成多层结构的木材单板和玻璃纤维无纺布，所述木材单板与玻璃纤维无纺布之间通过异氰酸酯或者环氧树脂类胶粘剂粘接。2.根据权利要求1所述的木建筑承重梁柱，其特征在于：所述木材单板的纤维纵向与承重梁柱的轴向方向一致。3.一种如权利要求1所述的木建筑承重梁柱的生产方法，其特征在于：包括以下步骤：1)将旋切后的木材单板干燥至含水率8-10%，将干燥后的单板按要求拼宽（宽度等于梁柱的高度），将单板以同...