The invention discloses a method for preparing composite material of aluminum enamel frame, aluminum enamel, aluminum and / or Aluminum Alloy aggregate to form powder, mixing the powder material; mixed cold pressed into the cold forming billet billet; sintering billet (for different tonnage hot extrusion machine); parison sintered by hot extrusion machine extrusion product profiles. The invention of aluminum enamel composite materials with excellent comprehensive performance, can withstand 400 500 degrees high temperature, anti oxidation performance is excellent; the production cost is low, the comprehensive performance of the aluminum enamel composite material is excellent, the production cost is low, is an ideal substitute material of aluminum, Aluminum Alloy, can be widely used in the field of oven and other kitchen utensils.
【技术实现步骤摘要】
一种用于炉架的铝搪瓷复合材料制备方法
本专利技术属于铸造
,具体涉及一种用于炉架的铝搪瓷复合材料制备方法。
技术介绍
铝或铝合金材料用途广泛,由于其综合性能较好、其可用于很多领域,但其生产制造成本较高,在一定程序上限制了铝、铝合金材料的应用。目前采用的树脂或高分子材料与填料组成的复合材料在某些领域中可部分替代铝或铝合金材料,但树脂或高分子材料作为粘合剂与填料组成的产品在耐高温性、导热性和其它物理性能方面不够理想,加之该类产品生产成本也偏高,将其用于某些领域同样存在一定的局限性。
技术实现思路
为了克服现有
存在的上述技术问题,本专利技术的目的在于,提供一种用于炉架的铝搪瓷复合材料制备方法,生产成本低,使铝合金有较好耐高温性、导热性,提高其它物理性能。本专利技术提供的一种用于炉架的铝搪瓷复合材料制备方法,包括以下步骤:1)将铝搪瓷40-60%,铝或/和铝合金20-35%、骨材10-18%以粉态的形式充分混合;2)将混合好的粉料冷压成坯;3)将冷成型的坯经200-600℃烧结成型坯(适合不同吨位的热挤压机);4)烧结后的型坯经热挤压机挤出商品型材。本专利技术提供的一种用于炉架的铝搪瓷复合材料制备方法,其有益效果在于,铝搪瓷复合材料综合性能优异、生产成本低廉,是一种理想的铝、铝合金替代材料,可在诸多领域中被广泛推广运用。具体实施方式下面结合一个实施例,对本专利技术提供的一种用于炉架的铝搪瓷复合材料制备方法进行详细的说明。实施例本实施例的一种用于炉架的铝搪瓷复合材料制备方法,包括以下步骤:1)将铝搪瓷60%,铝或/和铝合金22%、骨材18%以粉态的形式充分 ...
【技术保护点】
一种用于炉架的铝搪瓷复合材料制备方法,其特征在于:包括以下步骤:1)将铝搪瓷40‑60%,铝或/和铝合金20‑35%、骨材10‑18%以粉态的形式充分混合;2)将混合好的粉料冷压成坯;3)将冷成型的坯经200‑600℃烧结成型坯;4)烧结后的型坯经热挤压机挤出商品型材。
【技术特征摘要】
1.一种用于炉架的铝搪瓷复合材料制备方法,其特征在于:包括以下步骤:1)将铝搪瓷40-60%,铝或/和铝合金20-35%、骨材10-18...
【专利技术属性】
技术研发人员:李玉敏,
申请(专利权)人:青岛天地铸造有限公司,
类型:发明
国别省市:山东,37