一种弱碱性金属加工润滑剂制造技术

本发明专利技术提供一种弱碱性金属加工润滑剂。传统金属加工高温润滑剂易造成黑色或白色污染。本发明专利技术组成原料重量百分配比为：硼酸钠15～70%、磷酸钠10～50%、可溶性氧化硼0.5～30%，上述组成原料再加入10～15倍重量的水；该润滑剂的pH值为7～9。本发明专利技术具有良好的高温润滑性能，对钢管性能和钢管表面质量不产生负面影响，对环境不造成任何污染，是充分保护生产环境的绿色环保型润滑剂。

A weak alkali metal processing lubricant

The present invention provides a weak alkali metal processing lubricant. The traditional metal processing high temperature lubricants can cause black or white pollution. The weight distribution ratio of the raw material is as follows: sodium borate 15 ~ 70%, sodium phosphate 10 ~ 50%, soluble boron oxide 0.5 ~ 30%, and the raw material added above 10~15 times the weight of water, and the pH value of the lubricant is 7~9. The invention has good high temperature lubrication performance, has no negative effect on the performance of steel pipe and the surface quality of steel pipe, and does not cause any pollution to the environment. It is a green environmental friendly lubricant that fully protects the production environment.

【技术实现步骤摘要】
一种弱碱性金属加工润滑剂
本专利技术涉及一种弱碱性金属加工润滑剂，尤其涉及一种金属热塑性加工用环保型高温润滑剂及其使用方法，属于液体润滑剂的范畴。
技术介绍
在连轧钢管机组生产无缝钢管时，芯棒润滑是必不可少的工艺条件，芯棒润滑剂的质量优劣、性能好坏将直接影响到钢管质量、安全生产和环保。目前国内外使用的润滑剂大都以石墨微粉作为基本的润滑材料，再添加其它无机化合物和有机化合物。如中国专利公开号为CN1405286A、CN1493674A以及日本特开平2-51592号公报。由于把石墨微粉作为基本的润滑材料，就存在下列问题：①在轧制不锈钢或高合金钢时可能使钢管内表面被渗碳，会发生铬化物沿晶界沉淀，降低钢管的抗腐蚀性能；②石墨微粉有优良的导电性能，在使用润滑剂的过程中石墨微粉的污染会给电气设备、仪器仪表造成安全隐患；⑧给生产环境带来黑色污染。中国专利公开号为CN1243150A、CN1845982A、日本特开昭64-16894号公报、日本特开平5-171165号公报公开的这些润滑剂技术虽然不用石墨微粉作为润滑基料而改用天然或人造云母、蛭石、滑石粉、膨润土等微粉怍为润滑基料，但这仅仅是将白色污染本文档来自技高网...

【技术保护点】
一种弱碱性金属加工润滑剂，其特征在于组成原料重量百分配比为：硼酸钠 15～70%磷酸钠 10～50%可溶性氧化硼 0.5～30%上述组成原料再加入10～15倍重量的水；该润滑剂的pH值为7～9。

【技术特征摘要】
1.一种弱碱性金属加工润滑剂，其特征在于组成原料重量百分配比为：硼酸钠15～70%磷酸钠10～5...

【专利技术属性】
技术研发人员：俞为权，
申请(专利权)人：俞为权，
类型：发明
国别省市：江苏,32