The present invention relates to the technical field of wood adhesives, especially a kind of room temperature fast moisture curing wood adhesive and preparation method and application thereof, after the main agent selected ingredients and formulation, based on the composition of raw material selection and preparation of curing agent, which is stored separately, were prepared in the use process, and the main agent and curing agent quality than control, making it as wood gluing process used as adhesive, the bonding performance is excellent, and the less volatile components, reduce the environmental damage rate, improve the adhesive performance, improve the quality of wood adhesive.
【技术实现步骤摘要】
一种常温快速湿固化木材胶粘剂及其制备方法和应用
本专利技术涉及木材胶粘剂
，尤其是一种常温快速湿固化木材胶粘剂及其制备方法和应用。
技术介绍
随着工业的发展，胶粘剂的应用市场越来越广泛，品种也越来越多。目前，随着单组份胶粘剂缺点的日益凸显，双组份胶粘剂得到了快速的发展，主要有双组份溶剂型聚氨酯胶粘剂、双组份无溶剂型聚氨酯胶粘剂和热熔胶粘剂等，但在实质上，对于在粘接处理领域用的胶粘剂，大体可以分为两类：一类是天然高分子类胶粘剂，一类是合成高分子类胶粘剂，而合成高分子类胶粘剂是目前市场上研究较多的，而且对于该类胶粘剂的技术研究也比较多，如专利申请号为201610809225.0的湿固化聚氨酯热熔胶及其制备方法，公开以聚醚多元醇，聚酯多元醇，抗氧剂，增粘树脂，4,4’-二苯基甲烷二异氰酸酯，催化剂，硅烷偶联剂，白炭黑，磷酸等为原料制备成热熔胶粘剂，使得其具常规热熔胶优点外，更具有结皮时间长的优点，从而使产品在使用设备停机情况下的适应性更强。再如专利号为201410298003.8的低成型温度水性聚氨酯胶粘剂及其制备方法，公开基于低活化温度的水性聚氨酯乳液并配合聚氨...
【技术保护点】
一种常温快速湿固化木材胶粘剂，由主剂和固化剂双组份构成，其特征在于，主剂与固化剂的质量比为10:1，其中主剂的原料成分以质量份计为多亚甲基多苯基多异氰酸酯60份、二苯基甲烷二异氰酸酯20‑30份、聚酯多元醇10‑20份；固化剂的原料成分以质量份计为聚酯多元醇10份，有机胺0.1份。
【技术特征摘要】
1.一种常温快速湿固化木材胶粘剂，由主剂和固化剂双组份构成，其特征在于，主剂与固化剂的质量比为10:1，其中主剂的原料成分以质量份计为多亚甲基多苯基多异氰酸酯60份、二苯基甲烷二异氰酸酯20-30份、聚酯多元醇10-20份；固化剂的原料成分以质量份计为聚酯多元醇10份，有机胺0.1份。2.如权利要求1所述的常温快速湿固化木材胶粘剂，其特征在于，所述的二苯基甲烷二异氰酸酯为4，4'-二苯基甲烷二异氰酸酯，2，4'-二苯基甲烷二异氰酸酯、2，2'-二苯基甲烷二异氰酸酯中的一种或多种任意质量比混合。3.如权利要求1所述的常温快速湿固化木材胶粘剂，其特征在于，所述的聚酯多元醇为聚己二酸一缩二乙二醇酯二醇、聚己二酸乙二醇一缩二乙二醇酯二醇、聚己二酸乙二醇-1,4-丁二醇酯二醇、聚己二酸蓖麻油酯多元醇中的一种或者几种任意质量比混合。4.如权利要求1所述的常温快速湿固化木材胶粘剂，其特征在于，所述的有机胺为2，2'-二吗啉二乙基...
【专利技术属性】
技术研发人员：邹金鑫，张学敏，龙来早，苏占军，马福波，唐波，
申请(专利权)人：贵州省化工研究院，
类型：发明
国别省市：贵州,52