The invention discloses a \iron wall surface construction technology and material formula\, in particular, relates to a technology for making iron coated wall surface painting process and material formulation. Puzzle mode with magnetic puzzle in the plane with need iron or magnetic, and the magnetic post directly or iron plate on the wall, the puzzle area is small and not beautiful, the invention adopts latex paint and fine iron powder as the raw material formula, by scraping up leveling, grinding and other construction technology directly in production the color of iron wall with wall surface, for teenagers in the iron wall surface with jigsaw puzzle.
【技术实现步骤摘要】
铁性墙面施工工艺及材料配方
本专利技术涉及建筑装饰领域,具体来说,涉及一种涂装铁性墙面的材料配方及施工工艺。
技术介绍
带有磁性的智力拼图模形需要在带有铁性或磁性的平面上拼图,而直接在墙壁上用双面胶或铁钉固定张贴磁性或铁性的板显得麻烦而不美观,且板的面积较小。本专利技术采用乳胶漆和精铁粉为主要原材料配方,通过简易的施工工艺就可以在墙体表面制作带有铁性的彩色墙面,用于青少年在带有铁性的墙壁表面用带有磁性的益智拼图模型创作作品,解决了磁性的拼图模型在磁性的墙面上益智拼图,会因为磁性N极与S极的特性,出现异性相排的现象,使模型与模型之间缝隙不能贴合。
技术实现思路
针对相关技术中的上述技术问题,本专利技术提出直接在墙体表面施工,制作带有铁性的墙体表面层,为实现上述工艺技术目的,本专利技术的技术方案是这样实现的:铁性墙面施工工艺及材料配方包括:一、材料、配方1、腻子粉(泥浆)配方:双飞粉30kg、白水泥10kg、灰钙粉12kg、羟丙基甲基纤维素(HPMC)1kg、1250目精铁粉10kg,量取45kg水将材料分批倒入桶中搅拌,制成磁性腻子泥浆,备用,2、表面涂层配方:外墙用乳胶漆12kg、高岭土0.5kg、1250目精铁粉3.5kg,加适量水进行搅拌,直至材料成稀泥浆状,备用,二、施工工艺1.清理墙面→2.修补墙面→3.刮腻子→4.刮第一遍乳胶漆、刮第二遍乳胶漆、刮第三遍乳胶漆→5.刷第一遍彩色黑板漆、刷第二遍彩色黑板漆、刷第三遍彩色黑板漆,本专利技术的有益效果:1.直接在建筑墙体表面制作铁性墙面,与在墙体上粘贴或装钉磁性板相比,拼图平台面积大,操作方便,墙面整体美观 ...
【技术保护点】
铁性墙面施工工艺及材料配方,包括腻子粉(泥浆)配方,表面涂层配方。
【技术特征摘要】
1.铁性墙面施工工艺及材料配方,包括腻子粉(泥浆)配方,表面涂层配方。2.根据权利要求1所述的铁性墙面施工工艺及材料配方,其中腻子粉(泥浆)配方为,双飞粉30kg、白水泥10kg、灰钙粉12kg、羟丙基甲基纤维素(HPMC)1kg、1250目精铁...