The invention provides a kind of water resistant putty powder and a preparation method, which belongs to the field of filling material of the paint. The following components are as follows: according to the weight fraction of kaolin powder 35 50, 7, 5 montmorillonite hydroxypropyl methyl cellulose 2 5 copies, 0.7 copies, 0.1 polyacrylamide titanium dioxide 7 10 copies, two polydimethylsiloxane 1 3, 13 17, 2,2,4 sepiolite powder three methyl 1,3 pentanediol isobutyrate 0.3 single 7. The putty powder provided by the invention has high water resistance, acid and alkali corrosion resistance, change of cold and heat resistance, and high bond strength. It is safe and healthy, the material is easy to be obtained, and the cost is low, and the preparation method is simple.
【技术实现步骤摘要】
一种耐水腻子粉及其制备方法
本专利技术属于涂料的填充料领域，具体涉及一种耐水腻子粉及其制备方法。
技术介绍
耐水腻子粉主要目的是填充施工面的孔隙及矫正施工面的曲线偏差，为获得均匀、平滑的漆面打好基础。而耐水腻子粉作为其中的一个类别，主要用在有防水需求的墙面或物体表面。要求耐水、高粘结强度，以保证在空气中水蒸汽的长期侵蚀下不会出现空鼓、起皮、开裂等现象而仍然能够与基体紧密结合，不容易脱落。如果作为外迁涂料还需要耐酸碱，温度耐受范围大。目前，耐水腻子的耐水性、耐酸碱腐蚀性、耐冷热温度变化、粘结强度以及抗开裂性等提出了更高的要求。随着时代发展，人们健康生活的观念捉奸上升，目前环境友好型的耐水腻子粉尚未出现。
技术实现思路
所要解决的问题，本专利技术提供一种耐水腻子粉及其制备方法，腻子粉的耐水性、耐酸碱腐蚀性、耐冷热温度变化、粘结强度都很高。安全健康，材料容易获得，且成本低廉，制备方法简单。技术方案一种耐水腻子粉，由以下各组分按照如下重量分数组成：高岭土粉35-50、蒙脱土5-7、羟丙基甲基纤维素2-5份、聚丙烯酰胺0.1-0.7份、钛白粉7-10份、聚二甲基硅氧烷1-3份、海泡石粉13-17、2,2,4-三甲基-1,3-戊二醇单异丁酸酯0.3-7份。一种耐水腻子粉，由以下各组分按照如下重量分数组成：高岭土粉41、蒙脱土6、羟丙基甲基纤维素4份、聚丙烯酰胺0.5份、钛白粉8份、聚二甲基硅氧烷1份、海泡石粉15、2,2,4-三甲基-1,3-戊二醇单异丁酸酯5.6份。一种耐水腻子粉的制备方法，步骤一：称取各配料，备好；步骤二：混合粉碎；步骤三：加水搅拌铸模成为膏体；步骤四...
【技术保护点】
一种耐水腻子粉，其特征在于，由以下各组分按照如下重量分数组成：高岭土粉35‑50、蒙脱土5‑7、羟丙基甲基纤维素2‑5份、聚丙烯酰胺0.1‑0.7份、钛白粉7‑10份、聚二甲基硅氧烷1‑3份、海泡石粉13‑17、2,2,4‑三甲基‑1,3‑戊二醇单异丁酸酯0.3‑7份。
【技术特征摘要】
1.一种耐水腻子粉，其特征在于，由以下各组分按照如下重量分数组成：高岭土粉35-50、蒙脱土5-7、羟丙基甲基纤维素2-5份、聚丙烯酰胺0.1-0.7份、钛白粉7-10份、聚二甲基硅氧烷1-3份、海泡石粉13-17、2,2,4-三甲基-1,3-戊二醇单异丁酸酯0.3-7份。2.根据权利要求1所述的一种耐水腻子粉，其特征在于，由以下各组分按照如下重量分数组成：高岭土粉41、蒙脱土6、羟丙基甲基纤维素4份、聚丙烯酰胺0.5份...
【专利技术属性】
技术研发人员：王军红，
申请(专利权)人：南京一禾文化创意有限公司，
类型：发明
国别省市：江苏,32