The invention discloses a modified PTFE sealing filler and its preparation method, the material according to the weight percentage from 8 to 14% hydroxyl silicone oil and glass fiber powder from 12 to 20%, light calcium carbonate powder 5 ~ 7%, 2 ~ 5% carbon black high water absorbent resin of sodium polyacrylate, 6 to 10%, the balance of poly tetrafluoroethylene composition, its preparation method comprises the following steps: pretreatment of raw materials, grinding, mixing, molding, sintering and pressurized into blank, cooling, processed into finished products. The modified PTFE filled by adding modifier overcomes the shortcomings of traditional PTFE packing, such as poor compression creep resistance, poor expansion and recovery, and improved sealing performance.
【技术实现步骤摘要】
一种改性聚四氟乙烯密封填料及其制备方法
本专利技术涉及密封材料
，具体来讲涉及一种改性聚四氟乙烯密封填料及其制备方法。
技术介绍
聚四氟乙烯以其耐化学性、耐热性、耐寒性、耐油性优越于现在任何塑料而有“塑料之王”之称，它不易老化，不燃烧，吸水性近乎为零。其组织致密，分子结构无极性，用作填料，接触面可以做到平整光滑，对金属法兰不粘着，常见的有密封垫片、垫圈、密封带(条)、活塞环、导向环、密封环等，聚四氟乙烯垫片在无石棉垫片中是非常新颖的。由于石棉垫片已经逐渐淡出垫片市场，而无石棉垫片在极具腐蚀性和危险性化学环境中又无法达到与石棉垫片同等的性能，从而使聚四氟乙烯垫片备受青睐。但是聚四氟乙烯填料具有“冷流性”，即材料制品在长时间连续载荷作用下发生的塑性变形(蠕变)，如当聚四氟乙烯用作密封垫时，为密封严密而把螺栓拧得很紧，以致超过特定的压缩应力时，会使垫圈产生“冷流”(蠕变)而被压扁。由于聚四氟乙烯填料压缩强度低，用作垫片时，对于过于粗糙的法兰，聚四氟乙烯垫片往往不能密封，只能尽量选用更软的聚四氟乙烯垫片，而另一方面，对于很高的光洁度的法兰面，比如磨光过的表面，也是很...
【技术保护点】
一种改性聚四氟乙烯密封填料，其特征在于，由以下重量百分含量的组分制备而成：羟基硅油 8～14%玻璃纤维粉料 12～20%；轻质碳酸钙粉料 5～7%；碳黑 2～5%；聚丙烯酸钠高吸水树脂 6～10%；余量为聚四氟乙烯。
【技术特征摘要】
1.一种改性聚四氟乙烯密封填料，其特征在于，由以下重量百分含量的组分制备而成：羟基硅油8～14%玻璃纤维粉料12～20%；轻质碳酸钙粉料5～7%；碳黑2～5%；聚丙烯酸钠高吸水树脂6～10%；余量为聚四氟乙烯。2.如权利要求1所述的一种改性聚四氟乙烯密封填料，其特征在于，所述聚丙烯酸钠高吸水树脂为200～280mesh的粉粒。3.一种改性聚四氟乙烯密封填料的制备方法，其特征在于，包括下列步骤：（1）将固态原料捣碎，过目筛筛分，去除筛上物；筛分后在45～60℃下对粉料进行8～16h干燥预处理；（2）按重量百分比准确称量各原料，分别将固态粉料用研磨机充分研磨；（3）将原料在高速搅拌混合机内充分搅拌混合；（4）装模；（5）模具加压，经3～5分钟加压至30～38MPa，保持2～4分钟，后经6～8分钟...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。