The invention discloses a high flame retardant decorative paint, consists of the following components: weight of acrylic latex 25 30 copies, 6 copies of acrylic dispersant 4, quartz sand 8 10 copies, 15 copies, 10 mica Portland cement 16 18 copies, 4 copies, 2 diatomite methyl cellulose the water solution of 4 6 copies, 36 copies, 30 epoxy resin flame retardant 4 perchlorovinyl resin 7 copies, 6 copies, 3 vinyl acetate resin emulsion 2 9 copies, 12 copies of the 10 light calcium carbonate. The decorative paint with high flame retardancy performance is non-toxic and non polluting. It has environmental protection benefits, easy to store and store, convenient to use, good resistance performance and low insulation layer thickness.
【技术实现步骤摘要】
一种高阻燃性能装饰涂料
本专利技术涉及装饰涂料,具体是一种高阻燃性能装饰涂料。
技术介绍
随着科学技术的不断发展,人们对建筑材料提出了更高的要求,而目前使用于外墙的建筑材料在其各种性能上均不够理想,尤其在节能,防火,保温等方面不能满足需要,多数的外墙建筑材料均采用黑水泥作为猫结剂,比重大,导热系数大,而且戮结性能差,容易脱落,施工操作不易。随着人们生活水平的提高,人们对建筑物墙体的需求,己从单纯的保温性发展到兼具环保性,而对于建筑行业的人员来说,还考虑施工保温材料的好用性。目前市场用于建筑墙体上保温材料品种很多,这些材料具有较好的保温效果,但对环境有污染,并且存在施工复杂、占用卒问大的缺点。
技术实现思路
本专利技术提供了一种高阻燃性能装饰涂料,以解决上述技术问题。一种高阻燃性能装饰涂料,由以下重量份的成分组成:丙烯酸乳胶25-30份、丙烯酸分散剂4-6份、石英砂8-10份、云母粉10-15份、硅酸盐水泥16-18份、硅藻土2-4份、甲基纤维水溶液4-6份、环氧树脂30-36份、阻燃剂4-7份、过氯乙烯树脂3-6份、醋酸乙烯树脂乳液2-9份、轻质碳酸钙10-12份。优选的,所述的高阻燃性能装饰涂料,由以下重量份的成分组成:丙烯酸乳胶27份、丙烯酸分散剂5份、石英砂9份、云母粉13份、硅酸盐水泥17份、硅藻土3份、甲基纤维水溶液5份、环氧树脂33份、阻燃剂6份、过氯乙烯树脂5份、醋酸乙烯树脂乳液5份、轻质碳酸钙11份。本专利技术的有益效果:提供一种高阻燃性能装饰涂料,采用无毒无污染的材科组配,具有环保效益,易于保管、存贮,方便使用,阻性能好,保温层厚度小。具体实 ...
【技术保护点】
一种高阻燃性能装饰涂料,其特征在于,由以下重量份的成分组成:丙烯酸乳胶25‑30份、丙烯酸分散剂4‑6份、石英砂8‑10份、云母粉10‑15份、硅酸盐水泥16‑18份、硅藻土2‑4份、甲基纤维水溶液4‑6份、环氧树脂30‑36份、阻燃剂4‑7份、过氯乙烯树脂3‑6份、醋酸乙烯树脂乳液2‑9份、轻质碳酸钙10‑12份。
【技术特征摘要】
1.一种高阻燃性能装饰涂料,其特征在于,由以下重量份的成分组成:丙烯酸乳胶25-30份、丙烯酸分散剂4-6份、石英砂8-10份、云母粉10-15份、硅酸盐水泥16-18份、硅藻土2-4份、甲基纤维水溶液4-6份、环氧树脂30-36份、阻燃剂4-7份、过氯乙烯树脂3-6份、醋酸乙烯树脂乳液2-9份、轻...