用于汽车的防腐防锈油漆制造技术

本发明专利技术公开了一种用于汽车的防腐防锈油漆，按质量分数比包括：带锈防锈漆乳液9～15份、云母粉3～10份、催干剂5～12份、氧化锌3～6份、硅灰石粉7～8份、聚氯乙烯树脂4～9份、沸石粉3～10份、丙烯腈12～15份、溶剂10～16份,本发明专利技术的有益效果是：本发明专利技术防腐防锈油漆的原料简单，且成本较低，粉刷在金属上能有效避免因雨季或者长期暴晒导致的金属和油漆腐蚀和氧化，同时本发明专利技术的涂层硬度高，具有良好的耐候性和耐化学性能。

Anticorrosive and antirust paint for automobiles

The invention discloses a method for anti-corrosion of automobile paint, according to the mass fraction ratio includes: anti rust paint emulsion 9~15, mica powder 3~10 parts, driers 5~12, Zinc Oxide 3~6 copies, 7~8 copies, 4~9 copies of wollastonite, PVC resin, zeolite powder 3~10 copies, 12~15 copies, 10~16 copies of acrylonitrile solvent and the invention has the advantages that: the raw material of the invention is anti rust paint is simple, and the cost is low, paint can be avoided by the rainy season or long-term exposure to paint and metal corrosion and oxidation in the metal, the hardness of the coating of the invention is high and has good weathering resistance and chemical resistance.

【技术实现步骤摘要】
用于汽车的防腐防锈油漆
本专利技术涉及防腐防锈油漆，具体涉及用于汽车的防腐防锈油漆。
技术介绍
油漆是一种能牢固覆盖在物体表面，起保护、装饰、标志和其他特殊用途的化学混合物涂料。按照现代通行的化工产品的分类，涂料属于精细化工产品。现代的油漆的粉刷好以后不仅会传出一股刺鼻的味道，而且在一定的时间能不容易干，而且在粘性很差，粉刷在金属上，会与金属发生反应使金属氧化生锈。
技术实现思路
本专利技术的目的在于提供一种用于汽车的防腐防锈油漆，解决目前汽车使用油漆机稳定性不好、防锈效果不佳的问题。为解决上述的技术问题，本专利技术采用以下技术方案：用于汽车的防腐防锈油漆，按质量分数比包括：带锈防锈漆乳液9～15份、云母粉3～10份、催干剂5～12份、氧化锌3～6份、硅灰石粉7～8份、聚氯乙烯树脂4～9份、沸石粉3～10份、丙烯腈12～15份、溶剂10～16份。更进一步的技术方案是，上述中按质量分数比包括：带锈防锈漆乳液11～13份、云母粉5～8份、催干剂7～10份、氧化锌4～5份、硅灰石粉7～8份、聚氯乙烯树脂5～7份、沸石粉5～8份、丙烯腈13～14份、溶剂12～14份。更进一步的技术方案是，上述中本文档来自技高网...

【技术保护点】
一种用于汽车的防腐防锈油漆，其特征在于：按质量分数比包括：带锈防锈漆乳液9～15份、云母粉3～10份、催干剂5～12份、氧化锌3～6份、硅灰石粉7～8份、聚氯乙烯树脂4～9份、沸石粉3～10份、丙烯腈12～15份、溶剂10～16份。

【技术特征摘要】
1.一种用于汽车的防腐防锈油漆，其特征在于：按质量分数比包括：带锈防锈漆乳液9～15份、云母粉3～10份、催干剂5～12份、氧化锌3～6份、硅灰石粉7～8份、聚氯乙烯树脂4～9份、沸石粉3～10份、丙烯腈12～15份、溶剂10～16份。2.根据权利要求1所述的用于汽车的防腐防锈油漆，其特征在于：按质量分数比包括：带锈防锈漆乳液11～13份、云母粉5～8份、催干剂7～10份、氧化锌4～5份、硅灰石粉7～8份、聚氯乙烯树脂5～7份、沸石粉5～8份、丙烯腈13～14份、溶剂12～14份。3.根据权利要求2所述的用于汽车的防腐防锈油漆，其特征在于...