The invention overcomes the shortcomings of the existing technology, a lightweight ceramic substrate for production of solar tile is provided in order to solve the technical problem, the technical proposal of the invention is: a lightweight ceramic substrate for production of solar tile, which comprises a main material, feldspar, quartz and composite active ingredients, wherein the main ingredient of 25~35 copies, 45~55 copies of quartz feldspar, 15~25, composite active ingredient is 10~15, the composite active components including silicon carbide, magnesium carbonate and lithium carbonate; the main material, including shale, clay and kaolin, the shale, clay and kaolin by 1:1:1 mixed material, the composite material activity for any silicon, magnesium carbonate and lithium carbonate in a, or for a variety of combinations; the invention can be widely used in the field of light ceramic substrate.
【技术实现步骤摘要】
一种用于生产太阳能瓦的轻质陶瓷基材配方
本专利技术一种用于生产太阳能瓦的轻质陶瓷基材配方,属于轻质陶瓷基材
技术介绍
目前太阳能发电薄膜一般设置在玻璃夹层内进行利用,但玻璃基材不仅成本高,而且重量大,生产和安装均极为不便。
技术实现思路
本专利技术克服了现有技术存在的不足,提供了一种用于生产太阳能瓦的轻质陶瓷基材配方,降低了陶瓷砖的重量,并与太阳能发电薄膜结合,达到一物两用的目的,不仅将太阳能发电板的重量大大减小,而且生产和安装的成本均极低。为了解决上述技术问题,本专利技术采用的技术方案为:一种用于生产太阳能瓦的轻质陶瓷基材配方,包括主料、长石、石英和复合活性成分,其中,主料为25~35份,长石为45~55份,石英为15~25份,复合活性成分为10~15份,所述复合活性成分包括碳化硅、碳酸镁和碳酸锂。所述主料包括页岩、粘土和高岭土。所述页岩、粘土和高岭土按1:1:1混合配置主料。所述复合活性料为碳化硅、碳酸镁和碳酸锂中的任意一种,或为多种组合。本专利技术与现有技术相比具有的有益效果是:根据本专利技术生产出的产品坯体里有细微均匀的闭合孔,不但具有不透水、隔热功能,而且重量大大减轻,相同规格和厚度的情况下与传统工艺相比重量要轻二分之一以上,让产品重量大幅减轻的情况下,将轻质的陶瓷基材作为基层,用特种透明玻璃将太阳能发电薄膜压在基层上,可作为建筑材料覆盖到房顶,达到一物两用的目的,不仅将太阳能发电板的重量大大减小,而且生产和安装的成本均极低。具体实施方式本专利技术一种用于生产太阳能瓦的轻质陶瓷基材配方,包括主料、长石、石英和复合活性成分,其中,主料为25~ ...
【技术保护点】
一种用于生产太阳能瓦的轻质陶瓷基材配方,其特征在于:包括主料、长石、石英和复合活性成分,其中,主料为25~35份,长石为45~55份,石英为15~25份,复合活性成分为10~15份,所述复合活性成分包括碳化硅、碳酸镁和碳酸锂。
【技术特征摘要】
1.一种用于生产太阳能瓦的轻质陶瓷基材配方,其特征在于:包括主料、长石、石英和复合活性成分,其中,主料为25~35份,长石为45~55份,石英为15~25份,复合活性成分为10~15份,所述复合活性成分包括碳化硅、碳酸镁和碳酸锂。2.根据权利要求1所述的一种用于生产太阳能瓦的轻质陶瓷基材配方,其特征在...