The invention relates to a new corrosion resistant water permeable brick, according to the weight fraction ratio consists of the following components made of Portland cement: 34 superplasticizer 57 42 copies, 65 copies, 3 copies of anhydrite powder 2, 34 retarder 54, coagulation sludge powder 33 42, 23 43 binder a tree 4 6 terpene powder, air entraining agent 12 15 copies, 14 copies of slag powder 11, water 23 26, cenosphere 10 12 copies, 26 copies of 22 water glass, alkylphenol ether sulfosuccinate 14 16, 16 19 lignosulfonate copies of isocyanuric acid three glycidyl ester 3 5 copies, 34 copies of 23 quartz sand. The advantages of the invention are: the new corrosion resistant and permeable brick of the invention has higher porosity and permeability coefficient than that of conventional permeable bricks, and its compressive strength is still higher than that of conventional permeable bricks, and has good corrosion resistance and service life.
【技术实现步骤摘要】
一种新型耐腐蚀透水砖
本专利技术涉及建筑材料领域，特别涉及一种新型耐腐蚀透水砖。
技术介绍
城市人行道路多半铺设有砖块，以维持美观及平整性，现有人行道路上铺设的砖块大都使用粘土压制后直接烧结成型，其透水性能较差，其一方面阻断了雨水对地下水的补充，另一方面，由于雨水排泄不畅，也容易导致城市内涝。为了解决上述问题，现有技术中推出了透水砖产品。目前市场上的透水砖大致可分为陶瓷透水砖、水泥基透水砖和树脂结合透水砖三种基本类型。陶瓷透水砖虽然具有硬度高、强度大、花色丰富和尺寸规范的优势，但是，生产工艺复杂，资源消耗大，生产成本高；树脂结合透水砖则由于树脂的老化而引起耐久性差；水泥基透水砖生产成本低，但抗压强度低，且耐磨性差。而且对于普通的透水砖，由于其孔隙率较高，其耐盐腐蚀性差，从而导致耐久性与普通的粘土砖相差较大，需要更频繁的养护和更换作业。
技术实现思路
本专利技术要解决的技术问题是提供一种耐腐蚀效果好的新型耐腐蚀透水砖。为解决上述技术问题，本专利技术的技术方案为：一种新型耐腐蚀透水砖，其创新点在于：按重量分数配比由以下组分制成：硅酸盐水泥34-42份，减水剂57-65份，...
【技术保护点】
一种新型耐腐蚀透水砖，其特征在于：按重量分数配比由以下组分制成：硅酸盐水泥34‑42份，减水剂57‑65份，硬石膏粉2‑3份，缓凝剂34‑54份，混凝沉淀污泥粉33‑42份，粘结剂23‑43份，萜烯树脂粉4‑6份，引气剂12‑15份，矿渣粉11‑14份，水23‑26份，空心微珠10‑12份，水玻璃22‑26份，烷基酚醚磺基琥珀酸酯14‑16份，木质素磺酸盐16‑19份，异氰尿酸三缩水甘油酯3‑5份，石英砂23‑34份。
【技术特征摘要】
1.一种新型耐腐蚀透水砖，其特征在于：按重量分数配比由以下组分制成：硅酸盐水泥34-42份，减水剂57-65份，硬石膏粉2-3份，缓凝剂34-54份，混凝沉淀污泥粉33-42份，粘结剂23-43份，萜烯树脂粉4-6份，引气剂12-15份，矿渣粉11-14份，水23-26份，空心微珠10-12份，水玻璃22-26份，烷基酚醚磺基琥珀酸酯14-16份，木质素磺酸盐16-19份，异氰尿酸三缩水...
【专利技术属性】
技术研发人员：施路明，
申请(专利权)人：江苏闽江矿业有限公司，
类型：发明
国别省市：江苏,32