一种测定Gleeble高温压缩试样抗拉强度的方法技术
A method for measuring tensile strength of Gleeble high temperature compression specimen
The invention relates to a method for the determination of Gleeble high temperature compression tensile strength, the method of using wire cutting small cylindrical compression samples cut into I-shaped sample, after grinding and polishing process, the surface roughness of GB/T 228.1 2010 meet the tensile test method, tensile tests were carried out by tensile fixture made in the material testing machine, tensile strength has practical value. This method is more accurate and reliable than the traditional hardness value conversion method, and can be applied to the field of simulated rolling technology.
【技术实现步骤摘要】
一种测定Gleeble高温压缩试样抗拉强度的方法
本专利技术属于模拟轧制
，尤其涉及一种测定Gleeble高温压缩小圆饼试样抗拉强度的方法。
技术介绍
在金属类产品的研制和开发时，通常会先在热模拟试验机Gleeble上进行轧制模拟(高温压缩、高温拉伸)等系列试验，而由于做完高温压缩试验的样品太小(通常直径小于16mm)，所以，无法直接通过拉伸试验得到抗拉强度。目前，较常用的方法是根据GB/T1172-1999标准由实测的维氏硬度值换算得出抗拉强度值。硬度值换算方法是一种间接方式，虽然效率较高，但准确度难以判定，因此，以此作为指导力学性能的参数指标欠缺足够依据。
技术实现思路
本专利技术的目的在于提供一种测定Gleeble高温压缩试样抗拉强度的方法，为了实现上述目的，本专利技术采用如下技术方案：一种测定Gleeble高温压缩试样抗拉强度的方法，具体按以下步骤进行：1)取经过Gleeble高温压缩试验后小圆饼试样，用线切割沿径向将试样切割成厚度为1mm～2mm的薄片；2)用磨样机进行金相磨抛，使其表面呈抛光状态，表面粗糙度优于Ra1.6μm；3)用线切割切割成平行段...
【技术保护点】
一种测定Gleeble高温压缩试样抗拉强度的方法，其特征在于，具体按以下步骤进行：1)取经过Gleeble高温压缩试验后小圆饼试样，用线切割沿径向将试样切割成厚度为1mm～2mm的薄片；2)用磨样机进行金相磨抛，使其表面呈抛光状态，表面粗糙度优于Ra1.6μm；3)用线切割切割成平行段宽度为1mm～2mm，平行段长度为3mm，过渡圆弧R为1.5mm的工字型试样；4)用小型布砂轮将试样侧面进行打磨，使其表面粗糙度优于Ra1.6μm；5)将制好的试样装入与材料试验机匹配的自制夹具内，使其上下垂直，左右对中；6)设置材料试验机的工作参数，完成拉伸试验，得到实际的抗拉强度值。
【技术特征摘要】
1.一种测定Gleeble高温压缩试样抗拉强度的方法，其特征在于，具体按以下步骤进行：1)取经过Gleeble高温压缩试验后小圆饼试样，用线切割沿径向将试样切割成厚度为1mm～2mm的薄片；2)用磨样机进行金相磨抛，使其表面呈抛光状态，表面粗糙度优于Ra1.6μm；3)用线切割切割成平行段宽度为1mm～2mm，平行段长度为3mm，过渡圆弧R为1.5mm的工字型试样；4)用小型布砂轮将试样侧面进行打磨，使其表面粗糙度优于Ra1.6μm；5)将制好的试样装入与材料试验机匹配的自制夹...
【专利技术属性】
技术研发人员：岑风，张珂，褚峰，
申请(专利权)人：江苏省沙钢钢铁研究院有限公司，
类型：发明
国别省市：江苏,32