The invention discloses a preparation method of radiation proof fabric, the radiation proof fabric has at least two layers: the first layer is a fabric base, second layer components including 5 10 copies, 2 copies of the 1 nanoparticle adhesives, 3 5 silane coupling agent, 10 20 metal 50, 100 resin fiber. The invention of the radiation proof fabric anti radiation efficiency reached above 99%, and the second layer is very thin, about 0.03 0.05mm. The radiation protection fabric is simple, easy to operate, cheap and easy to obtain, and is harmless, harmless, not irritation to human body and low volatility. After finishing, its toughness, strength and handle are basically unaffected.
【技术实现步骤摘要】
一种防辐射织物的制备方法
本专利技术属于纺织
，更具体是涉及一种防辐射织物。
技术介绍
随着电气技术的进一步的发展，辐射在我们周围随处可见。不管是随处可见的手机、电脑、打印机，还是家用电器微波炉、电热毯、吹风机，都会有一定的辐射。虽然家用电器的辐射对于人的危害没有很大，但是当人体所处环境电辐射超过一定的强度或者产生一定的累积效应时，会对人体健康具有一定的损害，尤其是抵抗力较弱的老人、孩子，孕妇等。辐射的危害很多，比如：可导致儿童智力残缺；极可能是造成儿童患白血病的原因之一；能够诱发癌症并加速人体的癌细胞增殖；影响人的生殖系统，主要表现为男子精子质量降低，孕妇发生自然流产和胎儿畸形等；影响人们的心血管系统，表现为心悸，掉发，失眠，心动过缓，心搏血量减少，白细胞减少，免疫功能下降等等。目前市场上的防辐射织物，一般是用混纺金属纤维、导电纤维，成本高，不耐水洗，一部分人有过敏反应，因此，寻找一种耐用，舒适的防辐射织物是非常必要的。
技术实现思路
本专利技术的目的在于提供一种防辐射织物及制备方法，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：...
【技术保护点】
一种防辐射织物，其特征在于：所述防辐射织物至少有两层：第一层为织物基体；第二层的成分包括5‑10份纳米颗粒、1‑2份粘合剂、3‑5份硅烷偶联剂、10‑20份金属纤维、50‑100份树脂。
【技术特征摘要】
1.一种防辐射织物，其特征在于：所述防辐射织物至少有两层：第一层为织物基体；第二层的成分包括5-10份纳米颗粒、1-2份粘合剂、3-5份硅烷偶联剂、10-20份金属纤维、50-100份树脂。2.根据权利要求1所述的防辐射织物，其特征在于：所述的织物基体为针织织物、机织织物、非织造织物中的一种或是其中两种以上织物的组合；针织织物为经编织物或者纬编织物；机织织物为平纹织物、斜纹织物或者缎纹织物。3.根据权利要求1所述的防辐射织物，其特征在于：所述的纳米颗粒为纳米二氧化硅、纳米二氧化钛、纳米四氧化三铁、纳米氧化铝中的一种或者一种以上混合物。4.根据权利要求1所述的防辐射织物，其特征在于：所述的粘合剂为聚丙烯酸乳液、聚氨酯、甲基丙烯酸甲酯中的一种或者一种以上混合物。5.根据权利要求1所述的防辐射织物，其特征在于：所述的硅烷偶联剂为3-氨丙基三甲氧基硅烷、γ-(2,3-环氧丙氧)丙基三乙氧基硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷、N-(β-氨乙基)-γ-氨丙基三乙氧基硅烷、苯胺异佛尔酮和γ―氨丙基甲基二乙氧基硅烷中的任意一种或一种以上的混合物。6.根据权利要求...