一种使用丝素蛋白剥离制备二维纳米材料的方法技术
A method for the preparation of two-dimensional nanomaterials by using silk fibroin peeling
The invention provides a simple method for preparing two-dimensional nano materials, the use of natural, rich content of silk fibroin as stripping reagent, ultrasonic of graphite or black phosphorus and other layered materials (or shock) stripping, realize the scale for graphene layers or less black phosphorus two-dimensional nano material preparation at the same time, and gives the excellent biocompatibility and dispersion. Because the invention is the physical method of stripping, the prepared two-dimensional nanomaterials have good crystallinity. The preparation method of the invention has the advantages of simple process, low cost, no need for complex equipment, and green environmental protection.
【技术实现步骤摘要】
一种使用丝素蛋白剥离制备二维纳米材料的方法
本专利技术属于纳米材料制备以及生物医学应用领域，具体涉及使用羧基化处理的丝素蛋白溶液作为剥离试剂，制备单层或少层结构的二维纳米材料，形成的纳米材料具有优异的分散性和生物相容性，在生物医学领域具有重要的应用价值。
技术介绍
自2004年通过机械剥离首次发现石墨烯以来，二维纳米材料引起了广泛的关注和研究。众所周知，二维纳米材料的性能与其厚度具有密切的关系。单层或少层结构的二维纳米材料呈现出独特的力学、光学、电学等特征，成为当今研究的热点。到目前为止，除石墨烯以外，很多类石墨烯材料也受到越来越多的研究，如黑磷等。黑磷具有与石墨烯相类似的结构，表现出丰富的理化性质。近年来，单层或少层结构的石墨烯或黑磷二维纳米材料在药物递送、肿瘤诊断治疗、基因检测和生物传感等生物医学领域呈现出日益重要的应用价值。发展简便快速、性能可控、能够规模化生产的二维纳米材料制备新方法和新技术，是当前石墨烯或黑磷实用化需求中所亟待解决的热点问题。目前，二维纳米材料常用的制备方法有化学气相沉积法、湿化学合成法、液相剥离法等。考虑到其规模化生产和丰富的多样性，液...
【技术保护点】
一种使用丝素蛋白剥离制备二维纳米材料的方法，其特征在于：包括如下步骤：（1）制备羧基化处理的丝素蛋白溶液；（2）将步骤（1）得到的羧基化处理的丝素蛋白溶液与石墨或黑磷层状材料相混合，经超声或震荡进行剥离后得到小于十层的石墨烯或黑磷二维纳米材料。
【技术特征摘要】
1.一种使用丝素蛋白剥离制备二维纳米材料的方法，其特征在于：包括如下步骤：（1）制备羧基化处理的丝素蛋白溶液；（2）将步骤（1）得到的羧基化处理的丝素蛋白溶液与石墨或黑磷层状材料相混合，经超声或震荡进行剥离后得到小于十层的石墨烯或黑磷二维纳米材料。2.根据权利要求1所述的使用丝素蛋白剥离制备二维纳米材料的方法，其特征在于：包括如下具体步骤：（1）制备羧基化处理的丝素蛋白溶液，具体操作为：（a）蚕丝经脱胶、溶解、透析、过滤，制备成质量浓度为0.1%～50%的丝素蛋白水溶液；（b）将丝素蛋白水溶液与重氮盐反应，对丝素蛋白的酪氨酸残基进行羧基化修饰，然后与氯乙酸反应，对丝氨酸残基进行羧基化修饰，经透析，制备成质量浓度为0.1%～20%的羧基化处理的丝素蛋白溶液；（2）...