The invention discloses a high temperature grease and preparation method thereof, the grease includes lithium fatty acid soap 70 130 copies, 60 copies, 40 lauric acid 51, stearic acid 35 calcium soap thickener 49 72 copies and 36 copies of 18 graphite powder; the system of law the lithium fatty acid soap, lauric acid, stearic acid, calcium soap thickener and graphite powder at 25~50 DEG C mixing 1 10h, using three roller grinding machine are 0.5 3H evenly, can. The advantages of the high temperature grease has good oxidation stability, high temperature resistance and antiwear property, can be used as lubricating grease for high speed bearings; at the same time, the invention has the advantages of simple preparation process, no synthesis of complex equipment, reduce production cost, and reduce the load on the environment.
【技术实现步骤摘要】
一种耐高温润滑脂及其制备方法
本专利技术属于润滑脂领域，尤其涉及一种耐高温润滑脂及其制备方法。
技术介绍
润滑脂是工业润滑剂的重要组成部分，由于其本身固有的优良性能，不仅能满足一般的润滑要求，而且还具有良好的极压、抗磨和密封性能。广泛应用于钢铁、汽车、航空航天和军事等工业。
技术实现思路
专利技术目的：本专利技术的第一目的是提供一种具有良好的氧化安定性、耐高温性能和极压抗磨性的耐高温润滑脂；本专利技术的第二目的是提供该润滑脂的制备方法。技术方案：本专利技术的耐高温润滑脂，按重量份数计包括如下原料：脂肪酸锂皂70-130份、月桂酸40-60份、硬脂酸35-51份、钙皂稠化剂49-72份及石墨粉18-36份。优选的，脂肪酸锂皂90-120份；月桂酸45-55份；硬脂酸40-50份；钙皂稠化剂55-65份。本专利技术制备耐高温润滑脂的方法，包括如下步骤：将脂肪酸锂皂、月桂酸、硬脂酸、钙皂稠化剂及石墨粉在25～50℃下搅拌混合1-10h，利用三辊机研磨均化0.5-3h使之均匀，即可。有益效果：与现有技术相比，本专利技术的显著优点为：该耐高温润滑脂具有良好的氧化安定性、耐高温性能和极压抗磨性，能够用作高速轴承的润滑脂；同时，本专利技术的制备工艺简单，无需复杂的合成设备，降低了生产成本，并减轻了对环境的负荷。具体实施方式实施例1原料：脂肪酸锂皂90份、月桂酸45份、硬脂酸40份、钙皂稠化剂55份及石墨粉18份。制备方法：将脂肪酸锂皂、月桂酸、硬脂酸、钙皂稠化剂及石墨粉在25℃下搅拌混合10h，利用三辊机研磨均化0.5h使之均匀，即可。实施例2原料：脂肪酸锂皂120份、月桂...
【技术保护点】
一种耐高温润滑脂，其特征在于按重量份数计包括如下原料：脂肪酸锂皂70‑130份、月桂酸40‑60份、硬脂酸35‑51份、钙皂稠化剂49‑72份及石墨粉18‑36份。
【技术特征摘要】
1.一种耐高温润滑脂，其特征在于按重量份数计包括如下原料：脂肪酸锂皂70-130份、月桂酸40-60份、硬脂酸35-51份、钙皂稠化剂49-72份及石墨粉18-36份。2.根据权利要求1所述的耐高温润滑脂，其特征在于：所述脂肪酸锂皂90-120份。3.根据权利要求1所述的耐高温润滑脂，其特征在于：所述月桂酸45-55份。4.根据权利要...