一种双掺杂金红石相TiO2纳米棒的制备方法技术

一种双掺杂金红石相TiO2纳米棒的制备方法，属于TiO2纳米聚合体的技术领域，以碳化钛为原料，将其分散到水中，然后加入乙二胺，分散20‑30min，将分散后的料液加入到反应釜中，于温度170‑190℃下，反应5‑6h，取出，冷却至20℃，经离心、洗涤、干燥，得到双掺杂金红石相TiO2纳米棒。本发明专利技术制备方法简单，实现了一步合成掺杂C、N元素的金红石相TiO2纳米棒。

Preparation of a double doped rutile TiO2 nanorod

Nanorod preparation method of double doped rutile TiO2, which belongs to the technical field of TiO2 nano aggregates, with titanium carbide as raw materials, which is dispersed into water and then adding 20 30min, dispersion, the liquid will be dispersed into a reaction kettle, the temperature of 170 to 190 DEG C, reaction 5 6h, removed, cooled to 20 DEG C, by centrifugation, washing and drying, the double doped rutile TiO2 nanorods. The preparation method of the invention is simple and realizes one step synthesis of rutile TiO2 nanorods doped with C and N elements.

【技术实现步骤摘要】
一种双掺杂金红石相TiO2纳米棒的制备方法
本专利技术属于TiO2纳米聚合体的
，涉及金红石相TiO2纳米棒的掺杂，具体涉及一种双掺杂金红石相TiO2纳米棒的制备方法。本专利技术制备方法实现了一步合成掺杂C、N元素的金红石相TiO2纳米棒。
技术介绍
随着改革开放经济大潮席卷全国三四十年后，环境与能源问题严重制约了目前我国经济持续高速发展。近年来的材料学研究表明：TiO2作为一种宽带隙半导体，在光化学和光电池领域有许多优势，是解决上述两大难题的最佳优选材料。二氧化钛(TiO2)半导体功能材料，由于其低成本、无毒性、高表面活性和高稳定性等优点，被广泛应用于光催化、太阳能电池、电致变色效应器件，湿度传感器件、抗菌器件和自旋电子学器件等领域。但由于其禁带宽度为3.2eV，导致其仅能直接吸收小于388nm波长的太阳光，不能有效吸收可见光，从而限制了TiO2在实际光催化和光电转换中的应用。
技术实现思路
本专利技术为解决上述问题，提供了一种双掺杂金红石相TiO2纳米棒的制备方法，有效减小了TiO2能带带隙，拓宽了TiO2的吸光范围。本专利技术为实现其目的采用的技术方案是：一种双掺杂金红石相T本文档来自技高网...

【技术保护点】
一种双掺杂金红石相TiO2纳米棒的制备方法，其特征在于，以碳化钛为原料，将其分散到水中，然后加入乙二胺，分散20‑30min，将分散后的料液加入到反应釜中，于温度160‑180℃下，反应5‑6h，取出，冷却至20℃，经离心、洗涤、干燥，得到双掺杂金红石相TiO2纳米棒。

【技术特征摘要】
1.一种双掺杂金红石相TiO2纳米棒的制备方法，其特征在于，以碳化钛为原料，将其分散到水中，然后加入乙二胺，分散20-30min，将分散后的料液加入到反应釜中，于温度160-180℃下，反应5-6h，取出，冷却至20℃，经离心、洗涤、干燥，得到双掺杂金红石相TiO2纳米棒。2.根据权利要求1所述的一种双掺杂金红石相TiO2纳米棒的制备方法，其特征在于，碳化钛与乙二胺的质量体积比为(0.06g-0.30g)：(4mL-8mL)。3.根据权利要求1所述的一种双掺杂金红石相TiO2纳米棒的制备方法，其特征在于，分散到水中所用的水为蒸馏水，碳化钛与蒸馏水的质量体积比为(0.06g-0.30g)：(16mL...

【专利技术属性】
技术研发人员：张建平，张川，张千，张潇，
申请(专利权)人：河北麦森钛白粉有限公司，
类型：发明
国别省市：河北,13