本发明专利技术涉及一种电泳涂料，特别是一种电泳底面合一漆，包括以下组成与组分：环氧树脂30～40％，丙烯酸树脂40～57％，电泳漆助剂1～5％，复合醇醚1～2％，颜料5～15％，填料5～20％。本发明专利技术制得的电泳漆可以底面合一使用于汽车、自动车、机电、家电等五金件的涂装，表面比较平整，且具有较高的耐候性能和耐盐雾性能。

An electrophoretic bottom surface combination lacquer

The invention relates to an electrophoretic coating, in particular to an electrophoretic bottom surface lacquer, comprising the following components and components: epoxy resin 30 to 40%, acrylic resin 40 to 57%, electrophoretic paint assistant 1 to 5%, compound alcohol ether 1 to 2%, pigment 5 to 15%, filler 5 to 5. The electrophoretic paint prepared by the invention can be used on the bottom and the surface to be applied to the coating of hardware such as automobiles, automatic cars, electromechanical appliances, household appliances, etc. the surface is relatively smooth, and has high weathering resistance and salt spray resistance.

【技术实现步骤摘要】
一种电泳底面合一漆
本专利技术涉及电泳涂料生产领域，特别是一种电泳底面合一漆。
技术介绍
电泳底面合一漆分为阴极电泳和阳极电泳，电泳涂料作为一类新型的低污染、省能源、省资源、起作保护和防腐蚀性的涂料，具有涂膜平整，耐水性和耐化学性好等特点，容易实现涂装工业的机械化和自动化，适合形状复杂，有边缘棱角、孔穴工件涂装，目前被大量应用于汽车、自动车、机电、家电等五金件的涂装。电泳涂料及涂装法在20世纪60年代后获得工业应用，采用电泳涂料可以进行全封闭循环系统运行，涂料几乎100％利用。电泳涂料以水溶性或水分散性离子型聚合物为成膜物，被涂工件可以是阳极也可以是阴极；现有的漆膜耐盐雾性能和耐候性能不能兼得，需要配套面漆进行弥补，达不到经济和实用的要求。
技术实现思路
本专利技术为了克服上述技术问题的不足，提供了一种电泳底面合一漆，使得产品的表面比较平整，同时提高了产品的耐候性能。解决上述技术问题的技术方案如下：一种电泳底面合一漆，按质量百分比计，包括以下组成与组分：进一步地说，所述的电泳漆助剂为正丁醇和复合醇醚按照质量比为3:2的混合物。进一步地说，所述的复合醇醚为丙二醇甲醚、乙二醇丁醚、二乙二醇丁本文档来自技高网...

【技术保护点】
一种电泳底面合一漆，其特征在于，按质量百分比计，包括以下组成与组分：

【技术特征摘要】
1.一种电泳底面合一漆，其特征在于，按质量百分比计，包括以下组成与组分：2.根据权利要求1所述的电泳底面合一漆，其特征在于，所述的电泳漆助剂为正丁醇和复合醇醚按照质量比为3:2的混合物。3.根据权利要求1或2任一项所述的电泳底面合一漆，其特征在于，所述的复合醇醚为丙二醇甲醚、乙二醇丁醚、二乙二醇丁醚和二乙二醇甲醚按照质量比为1:1:1:1的混合物。4.根据权利要求1所述的电泳底面合一漆，其特...

【专利技术属性】
技术研发人员：刘广志，刘敏超，
申请(专利权)人：江苏皓月涂料有限公司，
类型：发明
国别省市：江苏,32