The invention discloses a method for preparing modified antimony oxide flame retardant material, the method includes: antimony oxide, alkaline CA bentonite and calcium carbonate, aluminate coupling agent, ten bromo two benzene ethane mixture for a period of time at a certain temperature, speed, the antimony oxide was modified. Modified antimony oxide. Then EVA, modified antimony oxide and plasticizer were heated and mixed in high speed centrifuge, and mixed materials were obtained, and extruded granulation mechanism was used to prepare the masterbatch. The method is simple in operation, and has the advantages of high mechanical strength, good mechanical properties, high impact resistance, high flame retardancy, low smoke emission and reduced melting and dropping.
【技术实现步骤摘要】
一种改性氧化锑制备阻燃材料的方法
本专利技术涉及阻燃材料领域，具体是一种改性氧化锑制备阻燃材料的方法。
技术介绍
目前，人们生活中需要用到阻燃材料的方面愈加广泛，如服装、石油、化工、冶金、造船、消防、国防等领域。阻燃材料是一种保护材料，能够抑制或者延滞燃烧且自己不燃烧或不容易燃烧的材料，有固体的如水泥、钢材、玻璃等材料，也有液态的，为阻燃剂涂在物体表面，它能保证在起火的时候不被烧着也不会使得燃烧范围加剧、扩大。氧化锑是应用广泛且效果良好的阻燃剂，适用于环氧树脂、聚氨酯、氯丁橡胶、聚苯乙烯、聚氯乙稀、聚酯等。氧化锑在燃烧初期,首先是熔融,在材料表面形成保护膜隔绝空气,通过内部吸热反应,降低燃烧温度。在高温状态下氧化锑被汽化,稀释了空气中氧浓度,从而起到阻燃作用。但是由于阻燃剂与高分子材料相结合时由于存在界面差异，所以他们的相容性较差，使材料的机械性能降低，因此对氧化锑需进行表面改性。且单独使用时用量要大，阻燃效果差，有发烟量大和产生熔融滴落的缺点，常与其他阻燃剂、消烟剂并用。中国专利（CN201410183840.6）公开的一种阻燃、耐高温环保电缆，没有对氧化锑进行...
【技术保护点】
一种改性氧化锑制备阻燃材料的方法，其特征在于，包括以下步骤：（1）氧化锑有机增容改性：6～10份氧化锑、3～7份碱性钙基膨润土、2～8份轻质碳酸钙、3～6份铝酸酯偶联剂、5～10份十溴二苯乙烷混合；改性温度110～160℃，转速为2500～4500rpm/min，搅拌时间3～5h，得到改性氧化锑；（2）母粒制备：100份EVA、4～8份改性氧化锑、0.5～2.5份增塑剂，在高速离心机中加热混合，转速 2500～4500rpm/min，温度控制在70～100℃，得到混合物料；转入挤出造粒机制备母粒。
【技术特征摘要】
1.一种改性氧化锑制备阻燃材料的方法，其特征在于，包括以下步骤：（1）氧化锑有机增容改性：6～10份氧化锑、3～7份碱性钙基膨润土、2～8份轻质碳酸钙、3～6份铝酸酯偶联剂、5～10份十溴二苯乙烷混合；改性温度110～160℃，转速为2500～4500rpm/min，搅拌时间3～5h，得到改性氧化锑；（2）母粒制备：100份EVA、4～8份改性氧化锑、0.5～2.5份增塑剂，在高速离心机中加热混合，转速2500～4500rpm/min，温度控制在70～100℃，得到混合物料；转入挤出造粒机制备母粒。2.根据权利要求1所述的一种改性氧化锑...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。