一种用于太阳能电池封装的EVA胶膜制造技术

一种用于太阳能电池封装的EVA胶膜，包括：乙烯‑醋酸乙烯的共聚物、硅烷偶联剂、交联固化剂、交联固化促进剂、稳定剂、紫外光吸收剂、光稳定剂；其中，硅烷偶联剂包括乙烯基三甲氧基硅烷和氨丙基三乙氧基硅烷；交联固化剂为过氧化甲酸叔丁酯；交联固化促进剂为三聚氰酸三烯丙酯；稳定剂为大分子稀土类配合物。本发明专利技术提供了一种用于太阳能电池封装的EVA胶膜，使用大分子稀土类配合物作为稳定剂，有机配体配位效率高，同时对混合使用乙烯基三甲氧基硅烷和氨丙基三乙氧基硅烷作为偶联剂，增强玻璃强度，也增加了封装膜和玻璃的粘结性能。

A EVA film for solar cell packaging

For a EVA film solar battery package includes: ethylene vinyl acetate copolymer, silane coupling agent, curing agent, curing agent, stabilizer, UV absorbers, light stabilizers; wherein, silane coupling agent including vinyl trimethoxy silane and aminopropyltriethoxysilane; curing agent for the oxidation of formic acid tert butyl ester; crosslinking curing agent for three cyanuric acid allyl ester; stabilizer for macromolecular complexes of rare earth. The present invention provides a method for EVA film solar cell package, the use of large molecular complexes of rare earth organic ligands as stabilizers, high efficiency, and the mixed use of vinyltrimethoxysilane and aminopropyltriethoxy silane as a coupling agent to enhance the strength of the glass, also increase the bonding performance of packaging film and glass.

【技术实现步骤摘要】
一种用于太阳能电池封装的EVA胶膜
本专利技术属于高分子材料
，具体涉及一种用于太阳能电池封装的EVA胶膜。
技术介绍
EVA是乙烯与醋酸乙烯酯的无规共聚物，分子链中第二单体乙酸乙烯酯(VA)的引入使其性能与均聚聚乙烯明显不同。受VA的影响，EVA的结晶性降低，极性、透明性和柔韧性提高，另外EVA加热熔融时具有良好的浸润性，冷却固化时绕曲性、抗应力开裂性和粘接性能较好，这些特征使其成为一种非常理想的封装材料，尤其是在夹层玻璃和太阳能电池封装方面应用广泛。专利CN102504715提供了一种太阳能电池EVA胶膜，包括乙烯-醋酸乙烯的共聚物、硅烷偶联剂、交联固化剂、交联固化促进剂、热稳定剂、增粘剂、抗氧剂、紫外光吸收剂、受阻胺类光稳定剂，其中热稳定剂为稀土类液体稳定剂，但是这种热稳定剂会影响透光率，在本专利技术中我们使用大分子的稀土配合物作为稳定剂，能够对EVA胶膜在可见光透过率影响小，且在胶膜中分散性好，与基质有很好的相容性，同时与小分子稀土配合物相比而言，大分子的有机配体配位效率也相对较高。专利CN103725210和专利CN103555214中也分别提供了一种太阳能电池封装的本文档来自技高网...

【技术保护点】
一种用于太阳能电池封装的EVA胶膜，其特征在于，包括以下重量份材料：

【技术特征摘要】
1.一种用于太阳能电池封装的EVA胶膜，其特征在于，包括以下重量份材料：其中，硅烷偶联剂包括0.1-2份乙烯基三甲氧基硅烷和0.1-1份氨丙基三乙氧基硅烷；交联固化剂为过氧化甲酸叔丁酯；交联固化促进剂为三聚氰酸三烯丙酯；稳定剂为大分子稀土类配合物。...