The invention belongs to the technical field of the manufacture of cable insulation sheath. The invention discloses a preparation method of PVC flame retardant insulation sheath, which comprises the following steps: flame retardant PVC plastic injection and solvent according to the weight ratio of 1:1.1 to 1.5 mixed evenly, then the main plastic injection molding; barrel temperature is 200~250 DEG C, mold temperature is 50~70 DEG C, holding pressure is 70 ~ 85MPa. The holding time was 6 ~ 9s. The flame retardant PVC insulation sheath prepared by the invention has excellent flame retardant effect and has the characteristics of smooth and fine surface, good softness and so on.
【技术实现步骤摘要】
一种阻燃PVC绝缘护套的制备方法
本专利技术涉及电缆绝缘护套制造
，尤其是涉及一种阻燃PVC绝缘护套的制备方法。
技术介绍
现有技术中，电缆行业通常使用PVC绝缘护套作为绝缘防护，而PVC绝缘护套采用PVC注塑料作为原料，但是由于PVC树脂的自身缺点，其阻燃性能较差，难以满足现有行业的需求；现有技术中也有一些具有阻燃作用的PVC电缆注塑料，但是其添加的阻燃助剂，有些是具有含有卤素的阻燃剂，具有较大的危害作用，另一些则阻燃效果较差；此外，现有的PVC电缆绝缘管材普遍较硬，难以适用于某些使用环境，通过添加现有的增塑剂改善其柔软度，则又会影响管材的阻燃性能；因此，急需一种能够制得既具有较好柔软度同时阻燃性能优异的PVC绝缘材料的阻燃PVC注塑料进而制得具有复合现有需求的阻燃PVC绝缘护套。
技术实现思路
为解决上述问题，本专利技术提供了一种能够制备获得阻燃效果优异并且具有产品表面光滑细腻、柔软度较好等特性的阻燃PVC绝缘护套的制备方法。为实现上述目的，本专利技术采用的技术方案如下：一种阻燃PVC绝缘护套的制备方法，包括以下步骤：将阻燃PVC注塑料与溶剂按重量比1：1....
【技术保护点】
一种阻燃PVC绝缘护套的制备方法，其特征在于包括以下步骤：将阻燃PVC注塑料与溶剂按重量比1：1.1～1.5混合均匀，然后注塑成型；主塑料桶的温度为200～250℃，成型模具的温度为50～70℃，保压压力为70～85MPa，保压时间为6～9s。
【技术特征摘要】
1.一种阻燃PVC绝缘护套的制备方法，其特征在于包括以下步骤：将阻燃PVC注塑料与溶剂按重量比1：1.1～1.5混合均匀，然后注塑成型；主塑料桶的温度为200～250℃，成型模具的温度为50～70℃，保压压力为70～85MPa，保压时间为6～9s。2.根据权利要求1所述的一种阻燃PVC绝缘护套的制备方法，其特征在于所述的阻燃PVC注塑料由以下方法制得：a）膨胀蛭石改性：将膨胀蛭石依次在盐酸溶液和水中各浸泡30～40分钟并烘干，然后将其加入到25～30℃的膨胀蛭石重量2～3.5倍的饱和碳酸铵溶液中，超声分散同时烘干，然后加入膨胀蛭石重量0.2～0.6倍的聚硅氧烷阻燃剂和膨胀蛭石重量0.3～0.5倍的硅烷偶联剂混合均匀，然后在60～70℃下干燥制得改性膨胀蛭石；b）配料：按PVC树脂80份、改性膨胀蛭石80～100份、复合橡胶20～35份、增塑剂5～8份、润滑剂6～9份、热稳定剂4～6份、流动性改性剂1～4份、成膜剂10～15份的重量份配比称取各组分；c）混料：将各组分混合...
【专利技术属性】
技术研发人员：李晓东，余立峰，赵亚琼，
申请(专利权)人：浙江威思康塑胶有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。