A method of making sintered insulating bricks and building blocks by making paper sludge is introduced. It is made from paper mill sludge produced by paper mill and washed, dehydrated, dried, crushed and sieved. The raw material of papermaking sludge is washed by water, then dehydrated and dried to a relative moisture content of less than 20%. After drying, the paper sludge is crushed and processed and screened through sieve mesh, which is finished product pore forming material. The hole making material is suitable for the preparation of the sintered insulation brick and block. The method of the invention uses industrial waste paper sludge, waste, protect the environment and save resources, realize the comprehensive utilization of resources to avoid the pollution of papermaking sludge, papermaking sludge landfill to the environment, has strong operability, low cost of equipment, raw materials etc..
【技术实现步骤摘要】
一种利用造纸污泥制备烧结保温砖、砌块造孔材料的方法
本专利技术涉及一种利用造纸污泥制备烧结保温砖、砌块造孔材料的方法，属于建筑材料领域。
技术介绍
造纸污泥是造纸行业产生的工业废弃物。造纸污泥目前的处理方式主要有填埋、焚烧、投海等，这些处置方式，都存在着二次污染、浪费能源、处理空间等问题。建筑行业的能耗约占全国能耗总量的30%，建筑行业已经成为中国主要耗能行业之一。在建筑能耗中，建筑物围护结构的热散失所占比重约77%，墙体占围护结构的比例最大，通过墙体散热（含空气渗透散热）占59.4%。因此，提高墙体材料的保温隔热性能是建筑节能的主要途径之一。烧结保温砖、砌块具有优良的保温隔热性能，是一种极具发展潜力的新型墙体材料。目前，烧结保温砖、砌块的制备主要集中在通过其外观设计、复合、孔洞率及孔结构优化来提高其保温隔热性能。复合式煤矸石烧结保温砖（专利号CN204126112U），它是在空心砖体内置EPS保温条板。保温砌块（专利号CN203160510U），它对砌块的孔洞进行设计，设置三个通孔，三个通孔的截面积相同，三个通孔的截面积之和占整个砌块截面积的30~70%，三个通...
【技术保护点】
一种利用造纸污泥制备烧结保温砖、砌块造孔材料的方法，其特征在于：它包括以下步骤：（1）造纸污泥原料经过水洗至pH=5~10；（2）将水洗后的造纸污泥进行脱水、烘干，烘干后造纸污泥的相对含水率小于20%；（3）将烘干后的造纸污泥进行破碎，经筛孔为2mm的筛网进行筛分，颗粒尺寸小于2mm的造纸污泥即得成品造孔材料。
【技术特征摘要】
1.一种利用造纸污泥制备烧结保温砖、砌块造孔材料的方法，其特征在于：它包括以下步骤：（1）造纸污泥原料经过水洗至pH=5~10；（2）将水洗后的造纸污泥进行脱水、烘干，烘干后造纸污泥的相对含水率小于20%；（3）将烘干后的造纸污泥进行破碎，经筛孔为2mm的筛网进行筛分，颗粒尺寸小于2mm的造纸污泥即得成品造孔材料。2.根据权利要求1所述的一种利用造纸污泥制备烧结保温砖、砌块造孔材料的方法，其特征在于：所述的烘干温度为80℃~120℃。3.一种由权利要求1所述利用造纸污泥制备烧结保温砖、砌块造孔材料的方法制备的造孔材料用于...
【专利技术属性】
技术研发人员：杨良，吴炎平，邵滨，郭立新，陈滔，