表针的耐腐蚀性能的检测方法技术
Detection method of the corrosion resistance of the hand
Including the detection method, the corrosion resistance of a hand: Deionized water; and the formation temperature of 30 DEG to 60 DEG with the deionized water in a confined space, the relative humidity is greater than or equal to 50RH% gas environment, the environment will be placed in the hands of gas for detection of corrosion resistance. The detection method of the corrosion resistance of the hands of the present invention, detection can be achieved on the hands and watch the surface decoration coating corrosion resistance. This detection method can detect hands and watch the surface decoration coating in the actual use of real corrosion resistance, easy operation and reliable results.
【技术实现步骤摘要】
表针的耐腐蚀性能的检测方法
本专利技术涉及材料技术，特别是涉及一种表针的耐腐蚀性能的检测方法。
技术介绍
目前国内外的手表中指针式手表占主导地位，手表表针是指针式手表不可或缺的部分，其制备材质主要有黄铜、铝及铁，黄铜主要用于制造时针和分针，铝因质量轻主要用于制造秒针，而铁主要用于制造高档的烧蓝手表表针。同时，为了丰富手表表针的色彩，手表表针通常需要进行表面处理，如水镀、真空镀、喷漆及涂夜光粉等。由于手表是在装配洁净车间装配出来的，有些高档手表还会在手表壳内注入氩气，因此手表表针在手表壳内几乎处于洁净空间内，因此对手表表针的表面处理要求较低，一般仅对颜色有要求，颜色符合要求即可。如今行业内仅会对手表表针及其表面的装饰涂镀层进行紫外光照射试验。然而，在手表实际佩戴使用过程中，因环境及个人佩戴习惯不同，手表壳的密封性会下降，致使空气中的水汽进入到表壳内与表针接触，使得手表表针发生腐蚀，因此，手表表针也要求具有一定的耐腐蚀性能。紫外光照射无法检测出手表表针及其表面的装饰涂镀层的耐腐蚀性能，而现在行业内表壳体及其附件耐腐蚀性能测试方法(①中性盐雾试验和②人工汗腐蚀试验，执行...
【技术保护点】
一种表针的耐腐蚀性能的检测方法，其特征在于，包括：提供去离子水；以及用所述去离子水在一密闭空间内形成温度为30℃至60℃，相对湿度大于等于50RH％的气体环境，将所述表针置于所述气体环境中进行耐腐蚀性能检测。
【技术特征摘要】
1.一种表针的耐腐蚀性能的检测方法，其特征在于，包括：提供去离子水；以及用所述去离子水在一密闭空间内形成温度为30℃至60℃，相对湿度大于等于50RH％的气体环境，将所述表针置于所述气体环境中进行耐腐蚀性能检测。2.根据权利要求1所述的表针的腐蚀性能检测方法，其特征在于，所述去离子水的电导率为1.0μS/cm至5.0μS/cm，pH值为6.0至7.0。3.根据权利要求1所述的表针的耐腐蚀性能的检测方法，其特征在于，使所述气体环境的相对湿度大于等于80RH％。4.根据权利要求1所述的表针的耐腐蚀性能的检测方法，其特征在于，将所述表针置于所述气体环境中的时间为24h至72h。5.根据权利要求1所述的表针的耐腐蚀性能的检测方法，其特征在于，所述用所述去离子水在一密闭空间内形成温度为30℃至60℃，相对湿度大于等于50RH％的气体环境，将所述表针置于所述气体环境中进行耐腐蚀性能检测的步骤包括：提供外杯和内杯，所述外杯的内径大于所述内杯的外...