A preparation method of antibacterial materials containing nano gold and silver
The invention belongs to the technical field of medicine and health, particularly relates to a method for preparing nano silver antibacterial material, which comprises the following steps: A, egg white mixed with gold uniform solution, the pH value is adjusted to 8 11, and reaction in a water bath, get the reaction mixture; B, to step A reaction mixture the liquid containing silver solution, and reaction in a water bath containing gold and silver nano antibacterial material, compared with the prior art, the invention of gold and silver containing nano antibacterial materials have high antibacterial activity, safe and reliable, conducive to wound healing, the preparation method is simple.
【技术实现步骤摘要】
一种含纳米金银抗菌材料的制备方法
本专利技术属于医药卫生
，尤其涉及一种含纳米金银抗菌材料的制备方法。
技术介绍
众所周知，在人体皮肤出现伤口后，很容易被细菌感染，引起化脓等诸多疾病，很难以治理，特别是一些耐药细菌的感染，甚至会导致死亡。因此，寻找抗菌范围广、可以杀死耐药菌且没有生物毒性的抗菌药物意义重大，所以研究更先进的抗菌材料，来实现安全有效的杀菌，防止细菌感染一直是人们努力的方向之一。目前有许多用于治疗伤口感染的药物，其中纳米材料因其自生具备的一些特殊性质在研究中备受瞩目。尤其是金银等贵金属纳米材料，生物相容性好，具有良好的抗菌性，稳定的荧光特性，在生物医学当中具有广阔的应用前景。如纳米金，当其尺寸在五纳米以下时，会发出很强的荧光，可用于细菌的指示，对细菌的存活量进行实时监测，以适时控制用药剂量，达到精准抗菌的效果。纳米银具有很强的抗菌性，可应用于伤口上细菌特别是耐药菌的清除，保证了伤口在无菌条件下的有效愈合，借助银纳米材料的优良特性，可以发展能杀死细菌尤其是耐药菌的抗菌材料。然而纳米银在具备强大的抗菌性的同时，也具有了一定的生物毒性，这使得其在生物材...
【技术保护点】
一种含纳米金银抗菌材料的制备方法，其特征在于，包括以下步骤：A、将蛋清与含金溶液混合均匀，调节pH值为8‑11，并在水浴中反应，得到反应混合液；B、向步骤A中反应得到的反应混合液加入含银溶液，并在水浴中反应得到含纳米金银抗菌材料。
【技术特征摘要】
1.一种含纳米金银抗菌材料的制备方法，其特征在于，包括以下步骤：A、将蛋清与含金溶液混合均匀，调节pH值为8-11，并在水浴中反应，得到反应混合液；B、向步骤A中反应得到的反应混合液加入含银溶液，并在水浴中反应得到含纳米金银抗菌材料。2.根据权利要求1所述一种含纳米金银抗菌材料的制备方法，其特征在于，在步骤A中，所述蛋清与所述含金溶液体积比为0.34：(10-12)。3.根据权利要求2所述一种含纳米金银抗菌材料的制备方法，其特征在于，所述含金溶液质量浓度为0.01-0.1％。4.根据权利要求3所述一种含纳米金银抗菌材料的制备方法，其特征在于，所述含金溶液为氯金酸、八氯化四金、氯化金、三氯化金、一氯化金中一种或几种的混合物。5.根据权利要求2所述一种含纳米金银抗菌材料的制备方法，其特征在于，所述蛋清为鸡蛋清...
【专利技术属性】
技术研发人员：蓝广芊，李庆，陆飞，余堃，卢必涛，
申请(专利权)人：重庆和其美科技有限公司，
类型：发明
国别省市：重庆,50