The invention discloses a conductive paste and a preparation method thereof containing graphene, the slurry composition comprises the following components by weight: 70 to 90, conductive resin 15 ~ 25, 30 ~ 40 organic solvent, dispersant 0.5 ~ 1.5; wherein, the conductive phase consists of the following materials by weight percentage 20 ~ 30%, 70 ~ 80% graphene nano copper powder. The conductive slurry prepared by the invention is not only higher than the nano copper powder without graphene, but also better than the commercial silver paste. The organic carrier made of special resin material makes the conductive paste have high adhesion. Graphene has high stability and is used in preparation of slurry to make the conductive slurry have good moisture resistance. The use of graphene conductive slurry to replace the current silver pulp reduces the cost.
【技术实现步骤摘要】
一种含石墨烯的导电浆料及其制备方法
本专利技术属于导电浆料领域，具体涉及一种含石墨烯的导电浆料及其制备方法。
技术介绍
石墨烯(Graphene)是一种由碳原子以sp2杂化方式形成的蜂窝状平面薄膜，是一种只有一个原子层厚度的准二维材料，所以又叫做单原子层石墨。由于其十分良好的强度、柔韧、导电、导热、光学特性，在物理学、材料学、电子信息、计算机、航空航天等领域都得到了长足的发展。石墨烯在室温下的载流子迁移率约为15000cm2/(V-s)，这一数值超过了硅材料的10倍，是目前已知载流子迁移率最高的物质锑化铟(InSb)的两倍以上。在某些特定条件下如低温下，石墨烯的载流子迁移率甚至可高达250000cm2/(V-s)。与很多材料不一样，石墨烯的电子迁移率受温度变化的影响较小，50～500K之间的任何温度下，单层石墨烯的电子迁移率都在15000cm2/(V-s)左右。石墨烯具有非常好的热传导性能。纯的无缺陷的单层石墨烯的导热系数高达5300W/mK，是目前为止导热系数最高的碳材料，高于单壁碳纳米管(3500W/mK)和多壁碳纳米管(3000W/mK)。当它作为载体时，它...
【技术保护点】
一种含石墨烯的导电浆料，其特征在于，所述浆料由下述成分按重量份组成：导电相70～90、树脂15～25、有机溶剂30～40、分散剂0.5～1.5；其中，所述导电相按重量百分比由以下材料组成：20～30％石墨烯、70～80％纳米铜粉。
【技术特征摘要】
1.一种含石墨烯的导电浆料，其特征在于，所述浆料由下述成分按重量份组成：导电相70～90、树脂15～25、有机溶剂30～40、分散剂0.5～1.5；其中，所述导电相按重量百分比由以下材料组成：20～30％石墨烯、70～80％纳米铜粉。2.根据权利要求1所述的一种含石墨烯的导电浆料，其特征在于，所述石墨烯的层数≤10，电导率＞10000S/m，所述纳米铜粉的平均粒径≤50nm，比表面积＞18m2/g。3.根据权利要求1所述的一种含石墨烯的导电浆料，其特征在于，所述树脂为低分子聚酰胺树脂、丙烯酸改性醇酸树脂、苯乙烯改性醇酸树脂、脲醛树脂中的两种或两种以上的混合物。4.根据权利要求1所述的一种含石墨烯的导电浆料，其特征在于，所述有机...
【专利技术属性】
技术研发人员：汪洋，
申请(专利权)人：江苏时瑞电子科技有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。