一种陶瓷用陶土配方及其漂洗工艺组成比例

本发明专利技术提供一种陶瓷用陶土配方及其漂洗工艺，涉及陶瓷领域，包括如下重量组分：高岭土45～55份、石英8～11份、废白瓷粉8～10份、钾长石14～16份、钠长石8～13份、氧化锆5～7份、碳化硅6～8份；本发明专利技术提供了一种陶瓷用陶土配方及其漂洗工艺，使得陶土更加细腻，无多余颗粒物；瓷土清洗后，分离成瓷土和水，减少瓷土内多余的水分；分离瓷土和水，可有效解决瓷土清洗损耗高、成本高的问题。

A pottery clay formula and its rinsing process

The invention provides a ceramic clay formulation and rinsing process, relates to the field of ceramics, which comprises the following components: weight 45 ~ 55 kaolin and quartz 8 ~ 11, 8 ~ 10 of waste porcelain powder, potassium feldspar 14 - 16, 8 - 13, sodium feldspar zirconia 5 ~ 7 from 6 to 8, silicon carbide; the invention provides the use of clay formula and rinsing process of a ceramic clay, which is more delicate, no excess clay particles; after cleaning, separated into clay and water, reduce excess water and water separation in clay; clay clay, which can effectively solve the problem of high loss, high cost of cleaning the problem.

【技术实现步骤摘要】
一种陶瓷用陶土配方及其漂洗工艺
本专利技术涉及陶瓷领域，具体涉及一种陶瓷用陶土配方及其漂洗工艺。
技术介绍
瓷土是陶瓷的主要原料，它是以产于世界第一窑厂的中国景德镇附近的高岭而得名的。后来由“高岭”的中国音演变为“Kaolin”，而成为国际性的名词。纯粹的瓷土是一种白色或灰白色，有丝绢般光泽的软质矿物。瓷土是由云母和长石变质，其中的钠、钾、钙、铁等流失，加上水变化而成的，这种作用叫作“瓷土化”或“高岭土化”。至于瓷土化究竟因何而起，在学术界中虽然还没有定论，但大略可以认为是长石类由于温泉或含有碳酸气的水以及沼地植物腐化时所生的气体起作用变质而成的。一般瓷土多产于温泉附近或石灰层周围，可能就是这个原因。瓷土的熔点约在1780℃左右，实际上因为多少含有不纯物质，所以它的熔点略为降低。纯粹的瓷土(高岭土)存量不多，而且所谓纯粹的瓷土，也没有黏土那样强的粘度。此外，还含有未变质的长石、石英、铁矿及其他作为瓷土来源的岩石的碎片。
技术实现思路
针对现有技术的不足，本专利技术提供了一种陶瓷用陶土配方及其漂洗工艺，使得陶土更加细腻，无多余颗粒物。为实现以上目的，本专利技术通过以下技术方案予以实现：一种本文档来自技高网...

【技术保护点】
一种陶瓷用陶土配方，其特征在于，包括如下重量组分：高岭土45～55份、石英8～11份、废白瓷粉8～10份、钾长石14～16份、钠长石8～13份、氧化锆5～7份、碳化硅6～8份。

【技术特征摘要】
1.一种陶瓷用陶土配方，其特征在于，包括如下重量组分：高岭土45～55份、石英8～11份、废白瓷粉8～10份、钾长石14～16份、钠长石8～13份、氧化锆5～7份、碳化硅6～8份。2.如权利要求1所述的陶瓷用陶土的漂洗工艺，其特征在于，所述瓷土的制作工艺具体步骤为：S1.从矿区采取瓷石；S2.瓷石用铁锤敲碎至鸡蛋大小的块状，再利用粉碎机打成粉状；S3.将瓷石粉用水浸泡10～12h，水的温度为40～50℃；S4.将浸泡后瓷石粉放入漂洗装置中进行漂洗，水的温度为45～50℃；S5.漂洗装置运动频率...