The invention discloses a poly lactic acid filament silk fabric and its preparation method, with PLA filament as weft yarn, or PLA filament and silk as warp and weft, including PLA filament linear density is 50 ~ 150dtex, single fiber line density is 1 ~ 2dtex, with 3/ 22.2/24.4dtex, silkworm silk 4/22.2/24.4dtex and 5/22.2/24.4dtex, and the appropriate twist according to the requirement of the product configuration, fabric of plain, three on the two right twill and five three fly on warp satin, 550 ~ 720 /10cm, 400 to 550 on the weft density /10cm weaving fabric, refined, washing and drying and shaping to obtain silk fabrics. The fabric is similar to pure silk fabrics in terms of moisture permeability, air permeability and wrinkle resistance. The handle style is similar to real silk, and it can be applied to all kinds of women's fashion, scarves and so on.
【技术实现步骤摘要】
聚乳酸长丝仿真丝绸面料及其制备方法
本专利技术涉及一类生物基合成纤维仿真丝绸面料及其制备方法，具体的说涉及一种聚乳酸(PLA)长丝仿真丝丝绸面料及其制备方法。
技术介绍
聚乳酸(PLA)是一种绿色环保生物基材料，以含糖(淀粉或蔗糖等)的生物质，如：玉米、甜菜、木薯和甘蔗等为原料，将淀粉糖化为葡萄糖，再经发酵而得到乳酸，最后在一定条件下聚合成聚乳酸。聚乳酸(PLA)是在1932年由高分子化学家卡罗·瑟斯在真空条件下加热乳酸生产小分子产品时发现。DuPont公司于1954年采用了新的聚合方法制备出了高分子量的聚乳酸，美国Cargill公司将聚乳酸成功地开发为一种新型纺织纤维。我国的聚乳酸工业起步较晚，1987年前后，上海工业微生物研究所、江苏省微生物研究所、天津工业微生物研究所等开展发酵法合成聚乳酸的研究。PLA短纤维的应用研究较早，其不仅可以制作纯纺纱，也可与其他纤维进行混纺。1998年，日本钟纺公司推出Lactron聚乳酸纤维与棉、羊毛及其他天然纤维混纺制成的新型纺织品“KaneboCornFiber”。1999年正式展出由Lactron纤维制成的纺织品。2000...
【技术保护点】
一种聚乳酸长丝仿真丝绸面料的制备方法，其特征在于，采用线密度为50～150dtex的聚乳酸长丝作为经纬纱，或者采用线密度为50～150dtex的聚乳酸长丝与桑蚕丝作为经纬纱交织，配置上机经密为540～720根/10cm，上机纬密为400～550根/10cm，并配置织物组织平纹、三上二下右斜纹或五枚三飞缎纹制成织物坯布，再经精炼、水洗和烘干定型制成面料成品。
【技术特征摘要】
1.一种聚乳酸长丝仿真丝绸面料的制备方法，其特征在于，采用线密度为50～150dtex的聚乳酸长丝作为经纬纱，或者采用线密度为50～150dtex的聚乳酸长丝与桑蚕丝作为经纬纱交织，配置上机经密为540～720根/10cm，上机纬密为400～550根/10cm，并配置织物组织平纹、三上二下右斜纹或五枚三飞缎纹制成织物坯布，再经精炼、水洗和烘干定型制成面料成品。2.根据权利要求1所述的聚乳酸长丝仿真丝绸面料的制备方法，其特征在于，所述聚乳酸长丝规格为50dtex/36f、50dtex/48f、75dtex/36f或75dtex/48f，其中单纤维的线密度为1～2dtex；所述桑蚕丝规格为3/22.2/24.4dtex、4/22.2/24.4dtex或5/22.2/24.4dtex。3.根据权利要求1所述的聚乳酸长丝仿真丝绸面料的制备方法，其特征在于，所述聚乳酸长丝仿真丝绸面料是指聚乳酸长丝仿真丝电力纺、聚乳酸长丝仿真丝斜纹绸、聚乳酸长丝仿真丝素软缎或聚乳酸长丝仿双绉中一种；其中针对所述聚乳酸长丝仿真丝电力纺制备方法如下：采用50dtex/36f的聚乳酸长丝为经纱，并配合50dtex/36f、50dtex/48f、75dtex/36f或75dtex/48f的聚乳酸长丝，或2.5捻/cm的3/22.2/24.4dtex的桑蚕丝为纬纱，或者采用2.5捻/cm的3/22.2/24.4dtex的桑蚕丝为经纱，并配合50dtex/36f、50dtex/48f、75dtex/36f或75dtex/48f的聚乳酸长丝为纬纱；配置平纹组织，并配置上机经密540根/10cm，上机纬密为250～300根/10cm，采用18号筘，3穿入，在剑杆织机或者喷气织机上织造坯布；针对所述聚乳酸长丝仿真丝斜纹绸制备方法如下：采用50dtex/36f聚乳酸长丝为经纱，并配合50dtex/36f、50dtex/48f、75dtex/36f或75dtex/48f的聚乳酸长丝，或2.5捻/cm的3/22.2/24.4dtex的桑蚕丝为纬纱；或者采用2.5捻/cm的3/22.2/24.4dtex的桑蚕丝为经纱，并配合50dtex/36f、50dtex/48f、75dtex/36f或75dtex/48f的聚乳酸长丝为纬纱；配置三上二下右斜纹组织，并配置上机经密600根/10cm，上机纬密400～550根/10cm；采用15号筘，4穿入，在剑杆织机或者喷气织机上织造坯布；针对所述聚乳酸长丝仿真丝素软缎制备方法如下：采用75dtex/36f聚乳酸长丝为经纱，并配合50dtex/36f、50dtex/48f、75dtex/36f或75dtex/48f的聚乳酸长丝，或者2.5捻/cm的3/22.2/24.4dtex、4/22.2/24.4dtex或5/22.2/24.4dtex的桑蚕丝为纬纱；或者采用2.5捻/cm的3/22.2/24.4dtex的桑蚕丝为经纱，并配合50dtex/36f、50dtex/48f、75dtex/36f或75dtex/48f的聚乳酸长丝为纬纱；配置五枚三飞缎纹组织，并配置上机经密720根/10cm，上机纬密400～500根/10cm，采用18号筘，4穿入，在剑杆织机或者喷气织机上织造坯布；针对所述聚乳酸长丝仿双绉制备方法如下：采用50dtex/36f聚乳酸长丝为经纱，并配合26捻/cm的3/22.2/24.4dtex的桑蚕丝、26捻/cm的75dtex/36f的聚乳酸长丝或26捻/cm的75dtex/48f的聚乳酸长丝中一种作为纬纱，或者采用2.5捻/cm的3/22.2/24.4dtex的桑蚕丝为经纱，并配合26捻/cm的75dtex/36f的聚乳酸长丝或26捻/cm的75dtex/48f的聚乳酸长丝为纬纱；其中纬纱按照2S2Z顺序织造，配置平纹组织，...