本发明专利技术涉及一种用制浆造纸废液制备防风固沙保水剂的方法，具体方案是将造纸制浆废液蒸发至固含量 20‑40％；将缩合剂、尿素和胶粉加入废液中，升温至110‑140℃反应3‑5h；然后加入交联剂反应 2‑4h；再加入淀粉反应 0.5‑2h，得到液体产品；在250‑400℃喷雾干燥得到固体产品。本发明专利技术所产生的防风固沙保水剂有吸水保水功能，喷施于沙地表面可形成固结层，有一定的固沙作用。

Preparation of air - proof and sand - fixing agent in the waste liquid of pulping and papermaking

The invention relates to a method for preparing windbreak SAP for pulping papermaking wastewater system, the specific scheme is the pulping waste liquor is evaporated to the solid content of 20 will 40%; condensing agent, urea and powder with waste liquid, heating to 110 DEG C 140 reaction of 3 5h; and then adding a crosslinking agent reaction 2 4h; add 0.5 starch reaction 2h, liquid products; in 250 400 DEG C spray drying to obtain solid products. The wind - fixing and sand - retaining agent produced by the invention has the function of water absorption and water retention, which can be applied to the surface of the sand to form a consolidation layer, and has certain sand fixing effect.

【技术实现步骤摘要】
制浆造纸废液制备防风固沙保水剂方法
本专利技术属化工领域，特别涉及造纸制浆废液综合利用制备防风固沙保水剂技术。
技术介绍
我国是世界上受沙漠化危害最严重的国家之一，沙漠及沙漠化土地面积在不断增加，每年因沙漠造成的直接经济损失越来越大，直接影响到人类的生存环境，沙尘暴发生次数逐年增加，直接威胁到祖国政治文化中心首都北京市，目前西北地区和内蒙古草原地区沙化日趋严重，防风、固沙、保水，改良土壤，爱护环境，保护生态，绿化沙漠已成为我国燃眉之急。现在常用的化学治沙材料约有几十种，如合成树脂、有机胶乳、高分子聚合物、乳化沥青等，这些产品虽固沙效果好，但成本高，难以生物降解，更难以与植物种植固沙措施相结合，不能大面积推广。造纸制浆时原料中有50％的木质素成分被溶于制浆废液中，制浆废液不处理直接排放，污染严重，国家虽加大了治理力度，但治理投资大，使企业不堪重负，而制浆废液中的木质素含有丰富的植物生长所需的有机养分。使用本专利技术用造纸制浆废液制备防风固沙保水剂可以节约资源，变废为宝，有利于环境保护，造福于社会及人类。
技术实现思路
本专利技术利用造纸制浆废液中所含的木质素与尿素、淀粉、缩合剂、交联剂等反本文档来自技高网...

【技术保护点】
一种用造纸制浆废液制备防风固沙保水剂的方法， 其特征在于包括以下步骤 ：a）将造纸制浆废液蒸发至固含量 20‑40％ ；b）将缩合剂、 尿素和胶粉加入废液中， 升温至 110‑140℃反应 3‑5h ；c）再继续加入交联剂反应 2‑4h ；d）然后加入淀粉反应 0.5‑2h， 得到液体产品e）将液体产品在 250‑400℃喷雾干燥得到固体产品。

【技术特征摘要】
1.一种用造纸制浆废液制备防风固沙保水剂的方法，其特征在于包括以下步骤：a）将造纸制浆废液蒸发至固含量20-40％；b）将缩合剂、尿素和胶粉加入废液中，升温至110-140℃反应3-5h；c）再继续加入交联剂反应2-4h；d）然后加入淀粉反应0.5-2h，得到液体产品e）将液体产品在250-400℃喷...