The invention belongs to the technical field of phase change energy storage material, in particular to a polymer based phase change energy storage material, and further discloses a preparation method. Polymer phase change the material, using paraffin as phase change materials, addition of expanded graphite and aluminum nitride as high conductivity materials, the porous properties of expanded graphite, the paraffin wax can be adsorbed on the graphite morphology in the pore shall be fixed, to avoid the paraffin phase change material in liquid solid phase change because of its liquidity and easy around material mixing problem; at the same time the energy storage materials with polymer matrix materials, prepared by the energy storage material can be processed into storage sheet, further expand the scope of application of the energy storage materials.
【技术实现步骤摘要】
一种聚合物基相变储能材料及其制备方法
本专利技术属于相变储能材料
，具体涉及一种聚合物基相变储能材料，并进一步公开其制备方法。
技术介绍
随着二十一世纪电子科技的蓬勃发展，电子设备越来越趋于微型化、高集成化和大功率化，各类电子元器件的热密度越来越高，储热和快速散热成为微电子元器件及设备技术发展的重要因素。相变材料(PCM-PhaseChangeMaterial)是一种能随温度变化而改变物理性质并能提供潜热的物质，其转变物理性质的过程称为相变过程。这时相变材料能够吸收或释放大量的潜热，是一种非常好的绿色节能环保性能载体。相变控温是指利用相变材料的相变过程来储存或释放热量，从而实现物体温度的控制过程。将相变控温和导热材料应用到微电子元器件及设备中，利用相变材料的固-液相变潜能来储存热能的储热技术，具有储能密度大，储-放热过程近似等温等优势，可以延长电子器件和设备的使用时间、满足电子器件更高、更快的运行速度；且整个控温过程方便易控制，得到广泛研究和应用。由于固-液相变材料在熔融后相变为液相，具有一定的流动性，并且易与周围物质发生掺混，在实际应用中受到限制，一般使用...
【技术保护点】
一种聚合物基相变储能材料，其特征在于，所述相变储能材料的制备原料包括：聚合物基体材料15‑25重量份、相变材料15‑25重量份、多孔填料30‑70重量份、导热填料20‑30重量份。
【技术特征摘要】
1.一种聚合物基相变储能材料，其特征在于，所述相变储能材料的制备原料包括：聚合物基体材料15-25重量份、相变材料15-25重量份、多孔填料30-70重量份、导热填料20-30重量份。2.根据权利要求1所述的聚合物基相变储能材料，其特征在于，所述相变储能材料的制备原料包括：聚合物基体材料20重量份、相变材料20重量份、多孔填料50重量份、导热填料25重量份。3.根据权利要求1或2所述的聚合物基相变储能材料，其特征在于，所述聚合物基体材料为数均分子量Mn为30000-40000的聚酯树脂。4.根据权利要求3所述的聚合物基相变储能材料，其特征在于，所述聚酯树脂选自聚己二酸乙二醇酯、聚己二酸丁二醇酯、聚癸二酸乙二醇酯、聚癸二酸丁二醇酯、聚对苯二甲酸乙二醇酯、聚对苯二甲酸丁二醇酯、聚间苯二甲酸乙二醇酯、聚间苯二甲酸丁二醇酯中的至少一种。5.根据权利要求1-4任一项所述的聚合物基相变储能...
【专利技术属性】
技术研发人员：张长星，
申请(专利权)人：上海叹止新材料科技有限公司，华东理工大学，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。