The invention relates to a modified engineering plastics, especially engineering plastic imitation of metal material, is in general engineering plastics by weight percentage from 1% to 1.5%, add a particle size of 150 ~ 200nm of titanium dioxide, can keep stable dimensional change to extrusion molding, with the goal of reliable home appliances. In order to make the home appliance product has strong aluminum sandblasting appearance, can be sprayed with a coarse powder paint on the surface of the substrate formed by extrusion molding, according to weight ratio was prepared by the following components: diameter 23 ~ 50 m 8 powder 12, leveling agent 0.12 0.18, thermoplastic propylene 65 acid resin 75, liquid wax 8 12 copies, 22 copies of 18 thinner; imitation metal decorative materials prepared by realistic effect can be achieved, professionals with no hands can accurately distinguish the material types of state.
【技术实现步骤摘要】
一种改性工程塑料
本专利技术涉及一种改性工程塑料，特别是工程塑料仿金属型材，属于一种改性工程塑料领域。
技术介绍
为了体现家电产品的外观高档、美观，通常将铝型材通过拉丝、喷砂、氧化等处理方式装饰在家电产品整个外表面或制作为装饰条安装在家电产品边框，使家电产品看起来具有金属型材的效果，高雅美观。也有采用非金属类材料类，通过注塑成型或板材裁剪，表面再丝印亮银油墨和电镀铬等方式来实现。用注塑成形方式实现的技术难度大和成本高，因机型多而要求的装饰条长度尺寸不一样，有12种之多，尺寸从600mm～16500mm不等；同一种设备加工装饰条的长度受限制。挤塑成型可以根据需要而确定装饰条长度，克服加工装饰条的长度受限制的问题。但是，采用挤塑方式成形的基材通常采用成本和机械物理性能较高的ABS塑料来实现，成本低廉的HIPS在挤塑时材料分子间的收缩率使得制备的材料尺寸精度受温度变化影响较大，不利于装饰件与家电稳定配合。
技术实现思路
本专利技术所解决的技术问题是提供一种成本较低，挤塑成型时尺寸变化保持稳定，与家电产品配合可靠的装饰用一种改性工程塑料。解决上述技术问题的技术方案是在工程塑料...
【技术保护点】
一种改性工程塑料，其特征在于：在HIPS塑料中添加粒度为150～200nm的钛白粉，按重量百分比计，其添加量为1％～1.5％。
【技术特征摘要】
1.一种改性工程塑料，其特征在于：在HIPS塑料中添加粒度为150～200nm的钛白粉，按重量百分比计，其添加量为1％～1.5％。2.仿铝合金金属喷砂效果装饰件，其特征在于：它是采用权利要求1所述一种改性工程塑料通过挤塑成型，然后在其表面喷涂铝粉油漆。3.根据权利要求2所述仿铝合金金属喷砂效...
【专利技术属性】
技术研发人员：何永娜，
申请(专利权)人：天津恩博华科技有限公司，
类型：发明
国别省市：天津,12