A low friction acrylic composite materials, the raw materials were divided into 40 acrylic powder 50, methyl methacrylate 30 50 copies, 1 copies, 0.6 activator inhibitor 0.001 0.003 copies, 1.5 copies, 0.25 initiator PTFE powder 5 20; the composite material the preparation method is mainly acrylic powder, initiator and PTFE powder mixed 2 5h mixture machine, get the composite powder mixture; methyl methacrylate, activator and inhibitor mixed evenly mixed solvent; the composite powder mixture is added to the mixed solvent evenly mixed, poured into a mold in a vacuum, < 10Pa, curing at room temperature under 30 DEG C for 20 60 150min release, is. The invention has the advantages of preparation at room temperature, simple process, convenient operation and low energy consumption. The prepared low friction acrylic matrix composite has the characteristics of low friction coefficient and low wear rate, and is suitable for shaft sleeve, gear and other fields.
【技术实现步骤摘要】
一种低摩擦亚克力基复合材料及制备方法
本专利技术属于材料
，特别涉及一种复合材料及其制备方法。
技术介绍
与金属基自润滑复合材料相比，聚合物基自润滑复合材料具有摩擦系数低耐腐蚀、质量轻等优点。随着科学技术的发展，通过在聚合物基体中引入微纳米润滑或抗磨颗粒，可以进一步改善聚合物基自润滑复合材料的减摩耐磨性能，因此，越来越多传统上应用金属基自润滑复合材料的领域正逐步被聚合物基自润滑复合材料所取代。中国专利CN1597771A公开一种聚甲醛基自润滑复合材料。中国专利CN104788950A、CN101864168A分别公开尼龙基自润滑复合材料，中国专利CN1958671A公开了一种聚合物基体为聚酰亚胺、聚苯硫醚、聚碳酸酯或聚甲醛的自润滑复合材料，中国专利CN1958671A公开了一种双马来酰亚胺基自润滑复合材料，中国专利CN1847310A公开了一种聚醚醚酮基自润滑复合材料。聚合物基自润滑复合材料通常采用热模压或热挤压成形，制备工艺及过程较为复杂，并且在制备过程必须加热到一定温度，增加了能源消耗。
技术实现思路
本专利技术的目的提供一种工艺简单、操作方便、能耗低的、可...
【技术保护点】
一种低摩擦亚克力基复合材料，其特征在于：其原料组分及重量组份为：亚克力粉体40‑50份、甲基丙烯酸甲酯30‑50份、活化剂0.6‑1.0份、抑制剂0.001‑0.003份、引发剂0.25‑1.5份、聚四氟乙烯粉体5‑20份。
【技术特征摘要】
1.一种低摩擦亚克力基复合材料，其特征在于：其原料组分及重量组份为：亚克力粉体40-50份、甲基丙烯酸甲酯30-50份、活化剂0.6-1.0份、抑制剂0.001-0.003份、引发剂0.25-1.5份、聚四氟乙烯粉体5-20份。2.根据权利要求1所述的低摩擦亚克力基复合材料，其特征在于：所述的聚四氟乙烯(PTFE)粉体粒径范围为5-20μm，所述活化剂为N,N-二甲基对甲苯胺，所述抑制剂为邻苯二酚，所述引发...
【专利技术属性】
技术研发人员：谷大鹏，张龙肖，陈素文，刘守耀，宋克峰，
申请(专利权)人：燕山大学，
类型：发明
国别省市：河北,13