Plastic water-based ink of the invention provides a suitable for high speed printing binder, the binder is composed of acrylate copolymer emulsion acrylate copolymer emulsion with hard and soft 0 45 DEG C, the glass transition temperature of 125 DEG C and has 65 glass transition temperature by 1 4:2 6 weight ratio of mixture soft and hard emulsion; emulsion is composed of monomer, crosslinking monomer and optionally volume regulator, multifunctional surfactant, water soluble acrylic resin molecular weight Mw between 4000 20000Da under the action of initiator by free radical emulsion polymerization reaction was obtained, which is a crosslinking monomer one or more N butyl acrylamide, N isobutyl acrylamide and N butoxy ethoxy N acrylamide or acrylamide. The printing ink made of the waterborne plastic ink connecting material of the invention is better than the existing water soluble ink for printing, so as to ensure the printing quality at high printing speed. The invention also provides a preparation method for the soft emulsion and hard emulsion in the joint.
【技术实现步骤摘要】
一种适用于高速印刷的水性塑料油墨连接料及其制备方法
本专利技术涉及一种油墨连接料，尤其涉及一种水性印刷油墨连接料，更具体是涉及一种适用于高速印刷且印刷基材为塑料薄膜，如BOPP膜、PE膜或PET膜等的水性塑料油墨连接料。本专利技术还涉及一种上述水性塑料油墨连接料的制备方法。
技术介绍
油墨连接料是印刷油墨的重要组成部分，是油墨的流体部分，油墨中的固体成分依靠连接料的润湿作用能够在制造过程中被研细，依靠其黏度完成印刷过程的传递转移，在印刷品上依靠连接料的干燥成膜性使印迹形成具有光泽的牢固墨膜而保护颜料。印刷油墨的流变性、黏度、干燥性、成膜性以及印刷性能，主要取决于连接料中树脂的性能。我国是印刷大国，每年印刷油墨耗量已逾百万吨，每年因印刷油墨引起火灾，中毒的事件屡屡发生，尤其在食品软包装行业常引起的中毒事件及不合格产品更引起国家食品安全监管部门的重视，因此2009年国家颁布了关于在软包装行业使用的膜材、印刷油墨等强制性的法律法规，从此杜绝了苯溶性油墨、酯溶性油墨在软包装领域的使用。目前我国食品软包装领域采用的印刷油墨大多是醇溶性油墨，由于醇溶性树脂应用了较多的醇、酯类...
【技术保护点】
一种适用于高速印刷的水性塑料油墨连接料，是由软乳液和硬乳液按1‑4:2‑6的重量比混合而成；其中，软乳液中丙烯酸酯共聚物具有 0 ‑ 45℃ 的玻璃化转变温度，软乳液是由包括如下各组分及重量份数通过自由基乳液聚合反应制得：丙烯酸丁酯(BA) 0‑5份丙烯酸异辛酯(EHA) 5‑15份甲基丙烯酸甲酯(MMA) 15‑20份甲基丙烯酸正丁酯(BMA) 0‑5份甲基丙烯酸异丁酯(IBMA)...
【技术特征摘要】
1.一种适用于高速印刷的水性塑料油墨连接料，是由软乳液和硬乳液按1-4:2-6的重量比混合而成；其中，软乳液中丙烯酸酯共聚物具有0-45℃的玻璃化转变温度，软乳液是由包括如下各组分及重量份数通过自由基乳液聚合反应制得：丙烯酸丁酯(BA)0-5份丙烯酸异辛酯(EHA)5-15份甲基丙烯酸甲酯(MMA)15-20份甲基丙烯酸正丁酯(BMA)0-5份甲基丙烯酸异丁酯(IBMA)0-5份交联单体0.50-2.00份分子量调节剂不使用或0.01-0.05份多功能性表面活性剂0.13-0.35份Mw在4000-8000酸值60-90水性丙烯酸树脂3-10份Mw在16000-20000酸值200-240水性丙烯酸树脂0.20-2.0份去离子水45-65份引发剂0.35-0.90份硬乳液中丙烯酸酯共聚物具有65-125℃的玻璃化转变温度，硬乳液是由包括如下各组分及重量份数通过自由基乳液聚合反应制得：丙烯酸丁酯(BA)1-5份甲基丙烯酸甲酯(MMA)10-35份甲基丙烯酸异丁酯(IMBA)10-25份交联单体0.50-2.00份分子量调节剂不使用或0.01-0.05份多功能性表面活性剂0.13-0.35份Mw在4000-8000酸值60-90水性丙烯酸树脂3-10份Mw在16000-20000酸值200-240水性丙烯酸树脂0.2-2.0份去离子水50-68份引发剂0.35-0.90份其中软乳液和硬乳液的交联单体为N-正丁基丙烯酰胺、N-异丁基丙烯酰胺、N-丁氧基丙烯酰胺或N-乙氧基丙烯酰胺中的一种或多种；软乳液的功能表面活性剂为烷基环氧乙烷和/或环氧丙烷的共聚物；硬乳液的功能表面活性剂为壬基酚聚氧乙烯(7-25)醚类、C4-C8仲醇聚氧乙烯(7-25)醚类或C2-C7烷基聚氧乙烯(7-25)醚类中的一种或多种。2.根据权利要求1所述的适用于高速印刷的水性塑料油墨连接料，其特征在于：所述软乳液中丙烯酸酯共聚物具有5-40℃的玻璃化转变温度，硬乳液中的丙烯酸酯共聚物具有70-120℃的玻璃化转变温度。3.根据权利要求1或2所述的适用于高速印刷的水性塑料油墨连接料，其特征在于：所述Mw在4000-8000酸值60-90水性丙烯酸树脂为广东龙湖科技股份有限公司出品的型号为LHSR-50的水性丙烯酸树脂或韩华公司出品的型号为Sloucryl-60L的纯丙型丙烯酸树脂；Mw在16000-20000酸值200-240水性丙烯酸树脂为广东龙湖科技股份有限公司出品的型号为LHSR-80的水性丙烯酸树脂或庄臣公司出品的型号为Joncryl-671的纯丙烯酸树脂。4.根据权利要求3所述的适用于高速印刷的水性塑料油墨连接料，其特征在于：所述软乳液的功能表面活性剂的表面张力是在26-35达因之间，浊点在38-60℃之间，HLB值在8-14之间，选自美国陶氏化学出品的型号为EcosurfTMLF-45的表面活性剂或德国克莱恩公司出品的型号为CO336的表面活性剂。5.根据权利要求4所述的适用于高速印刷的水性塑料油墨连接料，其特征在于：所述硬乳液的功能表面活性剂的表面张力26-35达因之间，浊点在38-60℃之间，HLB值在8-11之间。6.根据权利要求5所...
【专利技术属性】
技术研发人员：罗庚望，夏宇正，焦钰钰，郭超，
申请(专利权)人：广东龙湖科技股份有限公司，
类型：发明
国别省市：广东,44