The invention discloses an antistatic composite material and a preparation method thereof. The composite material comprises the following components: PP, Magnesium Oxide, neoprene, polyester fiber, PVC, ethyl methacrylate, polyethylene glycol, silicon dioxide, antistatic agent and toughening agent. The preparation method for the PP, Magnesium Oxide, PVC and polyester fibres mixed to obtain a mixture of a mixture; a reaction kettle, adding chloroprene rubber, ethyl methacrylate, in the protection of inert gas under the condition of keeping temperature after cooling, adding ethyl methacrylate, polyethylene glycol and toughening agent, mixing two, to obtain a mixture; the mixture of two, silica and antistatic agent after mixing by twin-screw extruder, anti-static composite material. The composite material provided by the invention has good mechanical properties and antistatic property.
【技术实现步骤摘要】
一种防静电复合材料及其制备方法
本专利技术属于材料领域，具体涉及一种防静电复合材料及其制备方法。
技术介绍
目前，随着人们对静电危害认识的不断深化，防静电变得越来越重要，特别是对于半导体产品，高集成化精密电子元件，组成和精密仪器设备，医疗设备以及化工产品等在存放、转运过程中，由于摩擦、撞击、外界电场和磁场的影响，容易产生静电，静电吸尘会影响产品的性能，且静电积累在合适的条件下会产生放电，引起产品失效或元件损坏，可能会造成极大的经济损失。传统上抗静电热塑性材料是采用内部添加和/或外部处理两种方法制造的。内部添加是在聚合物内部添加导电剂，包括金属及金属氧化物粉末、导电碳黑、离子型表面活性剂、导电纤维等材料添加导电纤维经挤出机螺杆剪切后，纤维的长径比保持率较低，纤维间彼此不能有效形成网络，从而影响导电性能，必须通过提高添加量来提高抗静电性能；添加阳、阴离子表面活性剂，材料对使用环境的湿度的依赖明显，湿度大时抗静电效果好，湿度小时则效果差;添加金属及金属氧化物粉末、导电碳黑等抗静电剂，添加量大、工艺性差、材料强度损失大、颜色单一。
技术实现思路
本专利技术的目的在于为了克服以...
【技术保护点】
一种防静电复合材料，其特征在于，包括以下重量份计的组分：PP15‑20份，氧化镁1‑2份，氯丁橡胶8‑15份，聚酯纤维2‑6份， PVC 3‑7份，甲基丙烯酸乙酯1‑3份，聚乙二醇4‑8份，二氧化硅1‑2份，抗静电剂5‑10份，增韧剂1‑3份。
【技术特征摘要】
1.一种防静电复合材料，其特征在于，包括以下重量份计的组分：PP15-20份，氧化镁1-2份，氯丁橡胶8-15份，聚酯纤维2-6份，PVC3-7份，甲基丙烯酸乙酯1-3份，聚乙二醇4-8份，二氧化硅1-2份，抗静电剂5-10份，增韧剂1-3份。2.根据权利要求1所述的防静电复合材料，其特征在于，聚乙二醇为聚乙二醇600。3.根据权利要求1所述的防静电复合材料，其特征在于，抗静电剂为抗静电剂SN。4.根据权利要求1所述的防静电复合材料，其特征在于，增韧剂为聚乙烯醇缩丁醛。5.权利要求1所述的防静电复合材料的制备方法，其特征在于，包括以下步骤：步骤1，按照重量份称取各组分；步骤...
【专利技术属性】
技术研发人员：冉宏敏，
申请(专利权)人：苏州纽东精密制造科技有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。