由再循环和可再生的成分形成的长纤维热塑性塑料制造技术

本发明专利技术提供了一种制模组合物配方，包括聚丙烯、玻璃纤维以及一种包括可再生的片状模塑组合物转移膜的聚丙烯替代品。该聚丙烯替代品以1至35总重量百分比存在，也可以包括天然纤维素纤维或粉末。本发明专利技术还提供了一种方法，该聚丙烯替代品被混合和均质，然后与聚丙烯和添加剂以及之后的玻璃纤维混合。在纯聚丙烯使用的量的削减方面，相比传统热塑性塑料玻璃纤维填充模具是有减少的。

Long fiber thermoplastic plastics formed by recirculating and renewable components

The invention provides a formulation for molding compositions, including polypropylene, glass fiber, and a polypropylene substitute including a renewable sheet molding composition transfer film. The polypropylene substitutes are present with a total weight of 1 to 35 and can also include natural cellulose fibers or powders. The invention also provides a method for mixing and homogenizing the polypropylene substitutes and then mixing with the polypropylene and the additives and the later glass fibers. In terms of the reduction in the amount of pure polypropylene, it is less than the traditional thermoplastic fiberglass filling mold.

【技术实现步骤摘要】
由再循环和可再生的成分形成的长纤维热塑性塑料本申请为申请日是2013.01.07、申请号是201380012567.4、专利技术创造名称是“由再循环和可再生的成分形成的长纤维热塑性塑料”的专利技术专利申请的分案申请。相关申请本申请主张提交于2012年1月6日的美国临时申请序列号61/583,808的优先权；据此，其内容通过引用的方式并入。
本专利技术通常涉及到热塑性制模组合物，特别是由再循环和可再生成分形成的压缩可塑的长纤维热塑性塑料。
技术介绍
聚丙烯(PP)是一种用于多种应用中的热塑性聚合物，包括：包装业、纺织业、塑料零件以及不同类型的可重复使用容器、实验室设备，以及汽车零部件。热塑性可塑制品包含强化纤维，特别是玻璃纤维以不断增加的频率应用于模具的生产中。在如汽车零部件的应用中，与纤维强化、低密度以及热塑性模具的生产量有关的强度使这些材料成为十分有诱惑力的选择。此类制品的高强度以及韧性提供了许多相对于传统钢冲压件的优点。此类制品是将玻璃纤维绳束与熔化的热塑性薄膜结合，在双带压力机或双螺杆挤压机中生产的。聚丙烯通常的被作为热塑性聚合物用于此类制品模具中。由于表面光洁度要求以及对制品本文档来自技高网...

【技术保护点】
一种制模组合物，包括：聚丙烯；唯一的纤维填料玻璃纤维；一种包括再循环片状模塑组合物转移膜的聚丙烯替代品，包括聚丙烯膜的载荷量在1至35的总重量百分比且膜厚度在0.5至1.5密耳之间，具有一包裹聚乙烯的表面并作为SMC树脂膏的苯乙烯屏障使用，所述的再循环片状模塑组合物转移膜被切成各种形状，包括长宽比为2‑1000：1的条，或多边形，且最长线性尺寸和最短线性尺寸之间纵横比在1‑2：1之间。

【技术特征摘要】
2012.01.06 US 61/583,8081.一种制模组合物，包括：聚丙烯；唯一的纤维填料玻璃纤维；一种包括再循环片状模塑组合物转移膜的聚丙烯替代品，包括聚丙烯膜的载荷量在1至35的总重量百分比且膜厚度在0.5至1.5密耳之间，具有一包裹聚乙烯的表面并作为SMC树脂膏的苯乙烯屏障使用，所述的再循环片状模塑组合物转移...

【专利技术属性】
技术研发人员：普罗比尔·库马尔·古哈，米夏埃尔·J·西瓦叶克，斯沃蒂·内奥吉，
申请(专利权)人：赛史品威奥唐山结构复合材料有限公司，
类型：发明
国别省市：河北,13