一种含有氧化铝和氧化锆的碱硅玻璃制造技术

本发明专利技术公开了一种含有氧化铝和氧化锆的碱硅玻璃，按摩尔百分比计，包括：SiO2为45‑80％，R2O为10‑30％，ZrO2+Al2O3为10‑25％；其中：ZrO2:Al2O3的摩尔比为1:4，R2O:(Al2O3+ZrO2)的摩尔比为1.0‑1.2。本发明专利技术在碱硅玻璃中引入了Al2O3和ZrO2，有效实现玻璃结构的重组与再造；通过上述组分和配比，使玻璃的熔化特性、成型特性和工艺特性均能得到兼顾，且本发明专利技术的玻璃具有相对优良的力学性能，韧性好，抗冲击，耐划伤。

A alkali silica glass containing alumina and zirconium oxide

The invention discloses an alkali silicate glass containing alumina and zirconia, Moore percentage, including: SiO2 45 80%, R2O 10 30%, ZrO2+Al2O3 was 10 25%; including: ZrO2:Al2O3 = 1:4, R2O: (Al2O3+ZrO2) molar ratio of 1 1.2. The introduction of Al2O3 and ZrO2 in alkali silica glass, the effective realization of restructuring and reconstruction of the glass structure; through the above components and ratio, the melting characteristics, glass forming characteristics and process characteristics can be taken into account, and the glass of the invention has relatively good mechanical properties, good toughness, impact resistance, resistance scratch.

【技术实现步骤摘要】
一种含有氧化铝和氧化锆的碱硅玻璃
本专利技术涉及玻璃
，尤其涉及一种含有氧化铝和氧化锆的碱硅玻璃。
技术介绍
碱硅玻璃(R2O-SiO2)是一种最为基础的二元玻璃体系，R2O为碱金属氧化物，具有较好的熔化特性，但是化学稳定性和力学强度不好，因此成为其致命弱点，即使采用复合碱金属氧化物(Li2O，Na2O，K2O)进行性能调节与改善，其性能提高也是相对有限。如果期望形成相对稳定的玻璃，一般要满足和控制R2O/SiO2的摩尔比<0.5，那么总体要求碱金属氧化物总量在碱硅玻璃总量中(R2O＝Li2O，Na2O，K2O)小于33mol％，才能符合成为玻璃的前提技术要求。碱硅玻璃(R2O-SiO2)在三维空间的结构基本是层状结构，只有玻璃化学组成相对合理时，受玻璃黏度阻力影响可以阻止析晶发生。但是在实际生产过程中，即使化学组成选择是恰当的，因冷却速度相对不合理，也会出现两个不混溶液相(SiO2成份相，Na2O成份相)。为了改善碱硅玻璃(R2O-SiO2)性能，传统方法是添加碱土金属氧化物RO，RO为CaO、MgO等，使用最多的化学成份是CaO，形成R2O-CaO-SiO2玻本文档来自技高网...

【技术保护点】
一种含有氧化铝和氧化锆的碱硅玻璃，其特征在于，按摩尔百分比计，包括：SiO2         45‑80％；R2O          10‑30％；ZrO2+Al2O3   10‑25％；其中：ZrO2:Al2O3的摩尔比为1:4，R2O:(Al2O3+ZrO2)的摩尔比为1.0‑1.2。

【技术特征摘要】
1.一种含有氧化铝和氧化锆的碱硅玻璃，其特征在于，按摩尔百分比计，包括：SiO245-80％；R2O10-30％；ZrO2+Al2O310-25％；其中：ZrO2:Al2O3的摩尔比为1:4，R2O:(Al2O3+ZrO2)的摩尔比为1.0-1.2。2.如权利要求1所述的含有氧化铝和氧...

【专利技术属性】
技术研发人员：田英良，杨宝瑛，孙诗兵，吕锋，李辉，
申请(专利权)人：北京工业大学，
类型：发明
国别省市：北京,11