一种镍基高温合金或不锈钢连接用含硅硼的中间层合金及其应用制造技术

本发明专利技术公开了一种镍基高温合金或不锈钢连接用含硅硼的中间层合金及其应用，属于高温合金和不锈钢连接技术领域。按重量百分含量计，该中间层合金化学成分为：硼：2～3.5％；硅：1～3％；钨：4～10％；铬：10～15％；铁：3～6％；镍为余量；该中间层合金为采用甩带法制备出的非晶箔带，将其在1050～1250℃用于镍基高温合金或不锈钢的瞬间液相连接，所用时间为100～240分钟。

A nickel based superalloy or stainless steel connection with silicon boron in the middle layer and its application

The invention discloses an intermediate layer alloy containing silicon and boron for nickel based superalloy or stainless steel connection and its application, belonging to the technical field of high alloy and stainless steel connection. According to the weight percentage, the intermediate layer alloy chemical composition: B: 2 ~ 3.5%; silicon: 1 ~ 3%; W: 4 ~ 10%: 10 ~ 15%; chromium; iron nickel: 3 ~ 6%; margin; the intermediate layer alloy by amorphous foils prepared with rejection method the connecting belt, at 1050 to 1250 DEG C for transient liquid nickel based high temperature alloy or stainless steel, used for 100 to 240 minutes.

【技术实现步骤摘要】
一种镍基高温合金或不锈钢连接用含硅硼的中间层合金及其应用
本专利技术涉及高温合金和不锈钢连接
，具体涉及一种镍基高温合金或不锈钢连接用含硅硼的中间层合金及其应用，该中间层合金适用于镍基高温合金或不锈钢的连接。
技术介绍
现代工业生产中大量使用到高温合金和不锈钢材料，在这些材料的应用过程中，不仅仅要考虑材料本身的强度等制备，同时也往往需要解决这些材料的焊接问题。但是由于高温合金和不锈钢材料的合金化程度较高，往往含有较多的合金元素，导致这些材料的焊接性能极差，产生焊接冷、热裂纹的倾向性较高，严重影响了构件的正常使用。目前，高合金化合金的焊接往往采用真空钎焊的方法。钎焊材料的设计是钎焊的关键。目前使用的钎料都为粉末钎料，这种钎料在使用时必须与一定量的粘结剂混合，以实现其成型，但由于有粘结剂的挥发，难以避免会在焊缝中形成气孔等缺陷；钎料合金的另一种成型方法是甩带法制备的非晶箔带，但这种方法对合金成分控制要求较高，复杂体系的合金很难成型出规则形状的非晶带。另外，目前钎料中较高含量的硼、硅和磷等元素，也严重影响了焊接强度。随着镍基单晶高温合金材料的应用推广，与其相关的加工技术也越来越引起重本文档来自技高网...

【技术保护点】
一种镍基高温合金或不锈钢连接用含硅硼的中间层合金，其特征在于：该中间层合金为镍基合金，按重量百分含量计，合金化学成分为：硼2～3.5％，硅1～3％，钨4～10％，铬10～15％，铁3～6％，镍为余量。

【技术特征摘要】
1.一种镍基高温合金或不锈钢连接用含硅硼的中间层合金，其特征在于：该中间层合金为镍基合金，按重量百分含量计，合金化学成分为：硼2～3.5％，硅1～3％，钨4～10％，铬10～15％，铁3～6％，镍为余量。2.根据权利要求1所述的含硅硼的中间层合金，其特征在于：所述中间层合金为非晶态箔带状，采用甩带法制备获得。3.根据权利要求2所述的含硅硼的中间层合金，其特...

【专利技术属性】
技术研发人员：刘纪德，李金国，孙元，李博，金涛，周亦胄，孙晓峰，
申请(专利权)人：中国科学院金属研究所，
类型：发明
国别省市：辽宁,21