The invention discloses a method for prolonging service life of the water tank type slag, both sides of the inner wall of square groove in the first square groove bottom surface and the bottom surface of the left and right sides of the uniformly welded anchor, anchor high 1.5 2cm, 5 7cm wide, then on the three surface of tank wall on the cover thickness of 30mm specifications of the hexsteel, then choose one casting of high temperature ceramic wear-resistant material on the needle containing hexsteel spraying or pouring a wear protection layer, wear protective layer thickness is 10mm, wherein the needle length is 8mm, the diameter of 0.5 1mm needle, needle weight the wear resistant pouring material weight 10%, 6 summer maintenance 8 hours can be put into use.
【技术实现步骤摘要】
一种延长水渣方型槽使用寿命的方法
本专利技术涉及一种延长水渣方型槽使用寿命的方法。
技术介绍
现水渣系统使用的方型槽一般采用18—24mm热轧钢板采用焊接方式制成，由于水渣系统的输送介质为渣水混合物，且作业温度较高（80℃左右），一般在使用9-12个月就会出现局部磨穿漏水、漏渣现象，越到后期磨穿频次越高，增加了维护工的劳动强度，增加了企业生产成本。
技术实现思路
本专利技术的目的在于提供一种延长水渣方型槽使用寿命的方法，能够延长水渣方型槽的使用寿命，降低生产成本。本专利技术的目的是这样实现的，一种延长水渣方型槽使用寿命的方法，首先在方型槽的底面以及底面左右两侧的方型槽两侧内壁上均布间隔焊接锚固件，锚爪高1.5-2cm，间宽5-7cm，然后在所述三面槽体内壁上覆盖厚度为30mm规格的龟甲网，龟甲网与所述的锚固件固定连接在一起。再选用其中含有钢针的耐高温陶瓷耐磨浇注料对龟甲网进行填充、浇筑、抹平构成耐磨防护层，耐磨防护层高出龟甲网的厚度为10mm，其中所述钢针的长度为8mm、钢针的直径为0.5-1mm，钢针的重量占所述的耐磨浇注料重量的10%，钢针与耐磨浇注料均匀搅拌在一起，夏季养护6-8小时即可投入使用；养护时，用湿麻袋或湿席子盖在浇注料表面并及时洒水以保持湿润状态。本专利技术通过在某钢铁公司第二高炉分厂B高炉南场方型槽试用，水渣方型槽的耐磨效果大幅度提高，至少可使用18个月以上，且可以重复喷涂使用，大大减少了更换方型槽时的人力、资材的投入，极大地降低了企业生产成本。具体实施方式一种延长水渣方型槽使用寿命的方法，首先在方型槽的底面以及底面左右两侧的方型槽两侧内壁...
【技术保护点】
一种延长水渣方型槽使用寿命的方法，其特征在于首先在方型槽的底面以及底面左右两侧的方型槽两侧内壁上均布间隔焊接锚固件，锚爪高1.5‑2cm，间宽5‑7cm，然后在所述三面槽体内壁上覆盖厚度为30mm规格的龟甲网，龟甲网与所述的锚固件固定连接在一起。
【技术特征摘要】
1.一种延长水渣方型槽使用寿命的方法，其特征在于首先在方型槽的底面以及底面左右两侧的方型槽两侧内壁上均布间隔焊接锚固件，锚爪高1.5-2cm，间宽5-7cm，然后在所述三面槽体内壁上覆盖厚度为30mm规格的龟甲网，龟甲网与所述的锚固件固定连接在一起。2.再选用其中含有钢针的耐高温陶瓷耐磨浇注料对龟甲...
【专利技术属性】
技术研发人员：于涛，
申请(专利权)人：宝钢集团新疆八一钢铁有限公司，
类型：发明
国别省市：新疆,65