A liquid metal cooling, the cooling liquid by the mass percentage of 5 18% 13 15% castor oil, castor oil, triethanolamine 15 26% sodium nitrate, 6 12% sodium nitrite, 3 8% polyvinyl alcohol, 25 38% 1 3% polyethylene glycol, defoaming agent, 1 3% fungicides and 15 30% deionized water mixture. The cooling fluid is made up of castor oil with a mass percentage of 7%, 14% castor oil, triethanolamine, 17% sodium nitrate, 8% sodium nitrite, 4% polyvinyl alcohol, 27% polyethylene glycol, 2% defoamer, 2% germicide and 19% deionized water. The invention has the advantages that the formula through the improvement of the components, combined with the production process, can be produced with high adaptability, excellent cooling capacity, cooling speed and compatibility of the cooling liquid, so as to improve the processing quality of products, and no pollution, with good environmental protection.
【技术实现步骤摘要】
一种金属冷却液
本专利技术涉及一种冷却液配方,特别是涉及一种金属冷却液。
技术介绍
目前,随着人们对金属制品质量要求越来越高,对金属加工的要求也随之升高,其中,冷却液作为金属切削中的重要助剂,其性能也是各大金属加工厂所研究的重点,然而,现在的金属冷却剂还存在着不同温度需要不同冷却液、冷却能力不佳、冷却速度慢、兼容性差等问题,从而降低了加工质量,在不增加制作成本的情况下,制作出来满足高性能要求的冷却液,是我们急需解决的问题。
技术实现思路
为了克服现有冷却液配方的不足之处,本专利技术提供了一种金属冷却液。本专利技术的技术方案是这样实现的。本方案的一种金属冷却液,所述冷却液由质量百分比为5-18%的蓖麻油、13-15%的蓖麻油三乙醇胺、15-26%的硝酸钠、6-12%的亚硝酸钠、3-8%的聚乙烯醇、25-38%的聚乙二醇、1-3%的消泡剂、1-3%的杀菌剂及15-30%的去离子水混合而成。所述冷却液由质量百分比为7%的蓖麻油、14%的蓖麻油三乙醇胺、17%的硝酸钠、8%的亚硝酸钠、4%的聚乙烯醇、27%的聚乙二醇、2%的消泡剂、2%的杀菌剂及19%的去离子水混合而成。本专利技术的有益之处在于:本配方通过对成分的改进,结合制作工艺,可以生产出具有高适应性、冷却能力优秀、冷却速度快、兼容性强的冷却液,从而提高加工质量,并且产品无污染,具有很好的环保效果。具体实施方式一种金属冷却液,由7kg的蓖麻油、14kg的蓖麻油三乙醇胺、17kg的硝酸钠、8kg的亚硝酸钠、4kg的聚乙烯醇、27kg的聚乙二醇、2kg的消泡剂、2kg的杀菌剂及19kg的去离子水混合而成,本品具有高适 ...
【技术保护点】
一种金属冷却液,其特征在于:所述冷却液由质量百分比为5‑18%的蓖麻油、13‑15%的蓖麻油三乙醇胺、15‑26%的硝酸钠、6‑12%的亚硝酸钠、3‑8%的聚乙烯醇、25‑38%的聚乙二醇、1‑3%的消泡剂、1‑3%的杀菌剂及15‑30%的去离子水混合而成。
【技术特征摘要】
1.一种金属冷却液,其特征在于:所述冷却液由质量百分比为5-18%的蓖麻油、13-15%的蓖麻油三乙醇胺、15-26%的硝酸钠、6-12%的亚硝酸钠、3-8%的聚乙烯醇、25-38%的聚乙二醇、1-3%的消泡剂、1-3%的杀菌剂及15-30%的去离...
【专利技术属性】
技术研发人员:王亮,
申请(专利权)人:天津市四海亨通自行车有限公司,
类型:发明
国别省市:天津,12