The invention discloses a PVC pipe calcium and preparation method thereof, wherein the PVC pipe is designed by using calcium carbonate powder prepared by calcite system, including the following steps: S1, the calcium content of more than 98% S2, calcite; cleaning materials; S3, the first crushing S4 and second times; check S5, broken; ultrafine grinding; S6, further grinding, adding coupling agent; S7, in powder then add lubricant and plasticizer. The invention has PVC pipe special calcium, which is modified to improve the properties of PVC pipes through a variety of additives. Its performance is excellent, it has many advantages, such as large amount of adding, low cost and so on.
【技术实现步骤摘要】
一种PVC管材专用钙及其制备方法
本专利技术涉及工业填料领域，主要涉及一种PVC管材专用钙及其制备方法。
技术介绍
碳酸钙作为橡胶、塑料制品的填料，可以提高制品的耐热性、耐磨性、尺寸稳定性、刚度及可加工性，并降低制品的成本，但是其表面有亲水性较强的羟基，呈现较强的碱性，这种亲水疏油的性质使得碳酸钙与有机高聚物的亲和性差，易形成聚集体，造成在高聚物内部分分散不均匀，从而造成两种材料间界面缺陷，直接应用效果不好。而且碳酸钙作为填料，其耐酸性、光滑度、白度等性能还有待进一步提高。因此，普通碳酸钙在PVC管材中若添加过量则会影响管材的性能。如何使碳酸钙能在保证PVC管材性能不变甚至能提高性能的条件下增加填料的用量，降低生产成本，是PVC管材生产领域中一直研究的热点。因此，现有技术还有待于改进和发展。
技术实现思路
鉴于上述现有技术的不足，本专利技术的目的在于提供一种PVC管材专用钙及其制备方法，旨在提供一种适用于PVC管材的碳酸钙粉，解决现有普通碳酸钙粉在PVC管材生产中存在添加量小、直接应用效果不好的问题。本专利技术的技术方案如下：一种PVC管材专用钙的制备方法，其中，所述...
【技术保护点】
一种PVC管材专用钙的制备方法，其特征在于，所述PVC管材专钙是采用方解石制备得到的碳酸钙粉，具体包括以下步骤：S1、原料精选：选用钙含量在98%以上的方解石；S2、清洗原料：将方解石清洗干净、风干；S3、第一次粗碎：将方解石破碎至3~5公分大小，用水冲洗，晾干；S4、第二次破碎复选：将方解石送入锤式破碎机，将方解石破碎至5目以内；S5、超细研磨：对方解石进行超细研磨，粉碎至细度D97为4.5μm；S6、继续研磨，添加偶联剂：在粉体中加入偶联剂，研磨10~20分钟；S7、在粉体中依次加入润滑剂和增塑剂：依次加入润滑剂和增塑剂，研磨10~30分钟。
【技术特征摘要】
1.一种PVC管材专用钙的制备方法，其特征在于，所述PVC管材专钙是采用方解石制备得到的碳酸钙粉，具体包括以下步骤：S1、原料精选：选用钙含量在98%以上的方解石；S2、清洗原料：将方解石清洗干净、风干；S3、第一次粗碎：将方解石破碎至3~5公分大小，用水冲洗，晾干；S4、第二次破碎复选：将方解石送入锤式破碎机，将方解石破碎至5目以内；S5、超细研磨：对方解石进行超细研磨，粉碎至细度D97为4.5μm；S6、继续研磨，添加偶联剂：在粉体中加入偶联剂，研磨10~20分钟；S7、在粉体中依次加入润滑剂和增塑剂：依次加入润滑剂和增塑剂，研磨10~30分钟。2.根据权利要求1所述的PVC管材专用钙的制备方法，其特征在于，所述偶联剂为锆类偶联剂、镁类偶联剂和锡类偶联剂中的一种或多...
【专利技术属性】
技术研发人员：李斌，
申请(专利权)人：广东玉峰粉体材料股份有限公司，
类型：发明