一种极寒型水泥胶合剂制造技术

本发明专利技术公开了一种极寒型水泥胶合剂，包括如下重量份的原料：水泥2份，石英砂0.8～1.1份，水0.45～0.52份，减水剂0.05～0.07份，硅灰0.25～0.30份，引气剂0.001～0.002份。本发明专利技术极寒型水泥胶合剂较通用型水泥胶合剂冻融耐受性能明显提高，降低了由水泥低温膨胀引起的钢脚、水泥胶合剂、瓷件、铁帽间的内应力作用，从而降低了瓷件破坏的可能性，从根本上降低了瓷绝缘子在陡波冲击下的故障概率。

An extremely cold type cement adhesive

The invention discloses a cold type cement adhesive, which comprises the following raw materials in weight portion: 2 portions of cement, quartz sand from 0.8 to 1.1, 0.45 to 0.52 parts of water, water reducing agent 0.05 ~ 0.07, 0.25 ~ 0.30 silica fume, air entraining agent 0.001 ~ 0.002. The cold type cement is universal cement freeze-thaw tolerance performance is significantly improved, reducing internal stress caused by the steel, cement, foot porcelain, the gossan by cement expansion so as to reduce the possibility of failure, the porcelain pieces, a low probability of failure in the porcelain insulator under the impact of steep wave down from the fundamental.

【技术实现步骤摘要】
一种极寒型水泥胶合剂
：本专利技术涉及一种极寒型水泥胶合剂，属于一种瓷绝缘子生产用料。
技术介绍
：随着电力工业的发展，超高压、大跨距、远距离输电得到了迅速普及。为满足电力实业的发展，特高压输变电技术对绝缘子提出了更高的要求，对每个元件都要求有更高的可靠性。水泥胶合剂是由水泥、集料、水按一定比例调配而成，水泥胶合剂在水化硬化的过程中强度逐渐增加。水泥胶合剂是电磁产品的重要组成部分，起着将瓷件与金属附件结成整体的作用，它的品质直接关系到绝缘子的性能、寿命和可靠性，目前电磁产品中，水泥胶合剂是最薄弱的环节，明显不能满足生产需求，尤其在北方地区的极寒环境下使用时，其耐冻融性能难以满足要求，水泥胶合剂在低温膨胀，钢脚、水泥胶合剂、瓷件和铁帽之间的内应力大，瓷绝缘子在陡波冲击下，极易发生破坏，出现故障。
技术实现思路
：为解决上述问题，本专利技术的目的在于提供一种耐冻融性能高、适于在极寒环境下使用的水泥胶合剂。本专利技术的目的由如下技术方案实施，一种极寒型水泥胶合剂，其包括如下重量份的原料：水泥2份，石英砂0.8～1.1份，水0.45～0.52份，减水剂0.05～0.07份，硅灰0.25～0.30本文档来自技高网...

【技术保护点】
一种极寒型水泥胶合剂，其特征在于，其包括如下重量份的原料：水泥 2份，石英砂 0.8～1.1份，水 0.45～0.52份，减水剂 0.05～0.07份，硅灰 0.25～0.30份，引气剂 0.001～0.002份。

【技术特征摘要】
1.一种极寒型水泥胶合剂，其特征在于，其包括如下重量份的原料：水泥2份，石英砂0.8～1.1份，水0.45～0.52份，减水剂0.05～0.07份，硅灰0.25～0.30份，引气剂0.001～0.002份。2.根据权利要求1所述一种极寒型水泥胶合剂，其特征在于，其包括如下重量份的原料：水泥2份，石英砂1份，水0.49份，减水剂0.06份，硅灰0.28份，引气剂0.0014份。3.根据权利要求1...

【专利技术属性】
技术研发人员：韩建军，钱文晓，张俊双，肖冰，郭金刚，刘辰，李硕，孟杰，王博，吴冠宇，王志军，
申请(专利权)人：国网内蒙古东部电力有限公司电力科学研究院，国家电网公司，内蒙古精诚高压绝缘子有限责任公司，
类型：发明
国别省市：内蒙古,15