The invention discloses a ceramic microsphere energy-saving tile adhesive, including Portland cement 350 450, silicon aluminum oxide hollow ceramic beads 50 100, quartz sand or river sand 450 550, redispersible latex powder 20 30 copies, 10 copies of 5 polyvinyl alcohol, starch ether 0.5 1.5 cellulose ether, 2 5 copies, 5 copies of 3 wood fiber. The invention also discloses the preparation method of the ceramic tile adhesive. The invention uses silica alumina hollow ceramic microspheres instead of some or all mineral sand in the traditional tile glue, which can improve the energy saving effect of the ceramic tile glue, improve the flexibility and enhance the bond strength, and improve the bonding quality of the ceramic tile.
【技术实现步骤摘要】
一种陶瓷微球节能瓷砖胶及其制备方法
本专利技术属于粘合剂领域，尤其是涉及一种陶瓷微球节能瓷砖胶及其制备方法。
技术介绍
中国瓷砖产量及销量已经位居世界第一，同时，中国的瓷砖也在不断发展中，主要是1、瓷砖的尺寸规格越来越大；2、瓷砖防污效果更好，渗透率更低；3、瓷砖的吸水率越来越低，瓷砖背面越来越光滑，粘结起来更加困难。瓷砖的产量增加及新品种(尺寸增加和吸水率变低)的出现，都对瓷砖粘贴材料提出了新的要求。瓷砖胶在中国市场应用已达数十年，应用过程中存在以下问题：(1)粘结强度不足，目前市场上大多数瓷砖胶不能满足国家标准JC/T547的最低粘结强度要求≥0.5MPa，对低吸水、大面积的瓷砖，如玻化砖或仿古砖，满足该要求也不能真正达到安全粘贴。尤其外墙瓷砖暴露在室外，天气和季节的变化将导致瓷砖表面温度的变化，这种变化将在瓷砖胶中产生较大的剪切力，导致瓷砖与墙体粘结的破坏，形成空鼓甚至脱落；(2)瓷砖胶柔韧性不足，由于在瓷砖粘贴体系中，存在三个不同的材质基层墙体、瓷砖胶及瓷砖。在长期使用过程中，由于温度、湿度的变化，三种材料的收缩变形是不一致的，这时就需要瓷砖胶具有一定的柔...
【技术保护点】
一种陶瓷微球节能瓷砖胶，其特征在于包括以下组分：硅酸盐水泥350‑450份，氧化硅铝中空陶瓷微珠50‑100份，石英砂或河砂450‑550份，可再分散乳胶粉20‑30份，聚乙烯醇5‑10份，淀粉醚0.5‑1.5份，纤维素醚2‑5份，木质纤维3‑5份。
【技术特征摘要】
1.一种陶瓷微球节能瓷砖胶，其特征在于包括以下组分：硅酸盐水泥350-450份，氧化硅铝中空陶瓷微珠50-100份，石英砂或河砂450-550份，可再分散乳胶粉20-30份，聚乙烯醇5-10份，淀粉醚0.5-1.5份，纤维素醚2-5份，木质纤维3-5份。2.根据权利要求1所述的陶瓷微球节能瓷砖胶，其特征在于：所述氧化硅铝中空陶瓷微珠的粒径为50-120微米，其抗压强度为60Mpa。3.根据权利要求1所述的陶瓷微球节能瓷砖胶，其特征在于：所述硅酸盐水泥的强度等级为42.5。4.根据权利要求1所述的陶瓷微球节能瓷砖胶，其特征在于：所述石英砂或河砂过70-140目。5.根据权利要求1所述的陶瓷微球节能瓷砖胶，其特征在于：所述可再分散乳胶粉为乙烯-醋酸乙烯酯共聚物。6.根据权利要求1所述的陶瓷微球节能瓷砖胶，其特征在于：所述聚乙烯醇的聚合度为2488。7.根据权...
【专利技术属性】
技术研发人员：赵潇武，胡玲霞，
申请(专利权)人：浙江大森建筑节能科技有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。