The invention discloses an antibacterial thermal insulation high strength mortar, which belongs to the field of building material. The high-strength mortar comprising by weight of cement components: 45 70 copies, 35 copies, 20 straw fiber 30 55 copies, 8 copies of 1 silica sand and quartz sand 12 18 copies, 4 copies, 1 in 18 ceramic powder 24, copper foam 20 35 a rare earth salt, 1 5 copies, 0.8 copies, 0.2 silver nitrate superplasticizer 1 5 copies, 3 copies of 0.5 latex powder, water 70 90. Compared with the existing technology, the high-strength mortar component of the invention has the advantages of environmental protection, simple preparation, good mechanical performance, long holding time, strong sterilization ability and low autogenous shrinkage rate.
【技术实现步骤摘要】
一种抗菌保温高强砂浆
本专利技术属于建筑材料领域，具体涉及一种抗菌保温高强砂浆。
技术介绍
现代工程使用的结构越来越复杂，环境也越来越多样化，对砂浆的各项性能的要求逐渐提高。传统砂浆一般采用硅酸盐水泥、黄砂和水组成，水仅用来提高流动性，不用水胶比来控制强度。现代砂浆技术有所发展，市售砂浆种类增加，但是大多数砂浆仍然为普通砌筑砂浆、保温砂浆，且保温材料多为膨胀聚苯板、挤塑聚苯板和发泡聚氨酯，然而此种材料环保性差，抗菌抑菌能力弱，作为建筑或装饰材料，会给人们的健康带来隐患。CN102701667B的中国专利公开了稻壳保温高强砂浆，具体公开了该高强砂浆包括以重量计普通硅酸盐水泥：12％-20％、粉煤灰：2％-3％、硅灰：1％-2％、水：30％-35％、稻壳：2％-3％、粉碎的建筑废料：30％-32％、重钙粉：3％-7％、可再分散性乳胶粉：0.3％-1％、纤维素醚：0.07％-0.12％。虽然该高强砂浆利用废弃的稻壳为原料制备的高强砂浆，具有保温性能和较高的强度，减少了水泥的用量，但该砂浆高收缩性影响其广泛使用。
技术实现思路
针对现有技术的不足，本专利技术的目的在于提供一种...
【技术保护点】
一种抗菌保温高强砂浆，其特征在于，包括以下按重量份数计的组分：水泥45‑70份、秸秆粉20‑35份、纤维30‑55份、硅砂1‑8份、石英砂12‑18份、中沙1‑4份、陶瓷粉18‑24份、泡沫铜20‑35份、稀土盐1‑5份、硝酸银0.2‑0.8份、减水剂1‑5份、乳胶粉0.5‑3份、水70‑90份。
【技术特征摘要】
1.一种抗菌保温高强砂浆，其特征在于，包括以下按重量份数计的组分：水泥45-70份、秸秆粉20-35份、纤维30-55份、硅砂1-8份、石英砂12-18份、中沙1-4份、陶瓷粉18-24份、泡沫铜20-35份、稀土盐1-5份、硝酸银0.2-0.8份、减水剂1-5份、乳胶粉0.5-3份、水70-90份。2.根据权利要求1所述的一种抗菌保温高强砂浆，其特征在于，包括以下按重量份数计的组分：水泥68份、秸秆粉32份、纤维48份、硅砂5份、石英砂14份、中沙3份、陶瓷粉22份、泡沫铜28份、稀土盐3份、硝酸银0.2份、...
【专利技术属性】
技术研发人员：周琴，
申请(专利权)人：苏州仲勉装饰有限公司，
类型：发明
国别省市：江苏,32