The present invention relates to boron oxide, more specifically, the invention relates to a preparation method of a boron oxide product, containing about 80 90% three two boron containing boron oxide oxidation products by boric acid heated to about 180 220 DEG C, the boric acid dehydration, and the formation of a melt is cooled solid glass products of melted glass; the solid glass can be crushed to produce particulate products; preferably boric acid in about 195 205 C heating. The method can be conveniently used for continuous process, which can be continuously added to the reactor through a heating mixer boric acid, the molten glass product is cooled to form a solid glass product, the product can be crushed to the size of the required range.
【技术实现步骤摘要】
一种氧化硼产品的制备方法
本专利技术涉及氧化硼,更具体地说本专利技术涉及一种氧化硼产品的制备方法。
技术介绍
三氧化二硼(化学式:B2O3)又称氧化硼,是硼最主要的氧化物。它是一种白色蜡状固体,一般以无定形的状态存在,很难形成晶体,但在高强度退火后也能结晶。它是已知的最难结晶的物质之一。熔融时可以溶解许多碱性的金属氧化物,生成有特征颜色的玻璃状硼酸盐和偏硼酸盐(玻璃),用于制取元素硼和精细硼化合物。也可与多种氧化物化合制成具有特征颜色的硼玻璃、光学玻璃、耐热玻璃、仪器玻璃及玻璃纤维、光线防护材料等。还可用作油漆的耐火阻烯添加剂和干燥剂。
技术实现思路
本专利技术提供一种含有约80-90重量%三氧化二硼。的含氧化硼产品的制备方法。该方法需要较低的温度,因此大大降低了能量的消耗。该方法非常适于连续工艺,这种工艺可以连续的方式,但无需在反应区域耐高温或者经受长的停留时间的专用设备来生产高度有用的含氧化硼的产品。本专利技术的方法包括将硼酸加热到温度为约180~220℃;优选加热到约195-205℃,其加热时间足以使硼酸脱水,并且生成含有约80-90重量%三氧化二硼;优选地含有约84-86%三氧化二硼的熔融玻璃,将生成的熔融态玻璃冷却形成一种固态玻璃状产物,它可接着采用例如在锤磨机或者轧碎机上研磨而粉碎生成粒状的无定型含氧化硼的产品,这种产品基本上没有被钠、硫酸盐和其它不希望有的杂质污染。本专利技术的典型步骤中,将硼酸连续加入被通过包裹在反应器周围的套的热油循环加热的反应器-混合器中,通过将熔体温度控制在约180-220℃的范围,将反应混合物保持呈流动状态;该混合物采用 ...
【技术保护点】
一种氧化硼产品的制备方法,其特征在于,含有重量比为80‑90%三氧化二硼的无定型含氧化硼产品的制备方法,其中包括:将硼酸在足以使该硼酸脱水形成含有重量为比80‑90%三氧化二硼的熔融态玻璃的时间内,在180‑220℃范围内的温度下加热,并冷却该熔融态玻璃以便形成固体玻璃状产品。
【技术特征摘要】
1.一种氧化硼产品的制备方法,其特征在于,含有重量比为80-90%三氧化二硼的无定型含氧化硼产品的制备方法,其中包括:将硼酸在足以使该硼酸脱水形成含有重量为比80-90%三氧化二硼的熔融态玻璃的时间内,在1...
【专利技术属性】
技术研发人员:李海栓,
申请(专利权)人:长葛市联发粮食专业合作社,
类型:发明
国别省市:河南,41